Metallurgy and Mechanics of Welding
This page intentionally left blank
Metallurgy and Mechanics of Welding Processes and Industrial Applications
Edited by Régis Blondeau
First published in France in 2001 by Hermes Science/Lavoisier in 2 volumes entitled “Métallurgie et mécanique du soudage” and “Procédés et applications industrielles du soudage” First published in Great Britain and the United States in 2008 by ISTE Ltd and John Wiley & Sons, Inc. Apart from any fair dealing for the purposes of research or private study, or criticism or review, as permitted under the Copyright, Designs and Patents Act 1988, this publication may only be reproduced, stored or transmitted, in any form or by any means, with the prior permission in writing of the publishers, or in the case of reprographic reproduction in accordance with the terms and licenses issued by the CLA. Enquiries concerning reproduction outside these terms should be sent to the publishers at the undermentioned address: ISTE Ltd 27-37 St George’s Road London SW19 4EU UK
John Wiley & Sons, Inc. 111 River Street Hoboken, NJ 07030 USA
www.iste.co.uk
www.wiley.com
© ISTE Ltd, 2008 © LAVOISIER, 2001 The rights of Régis Blondeau to be identified as the author of this work have been asserted by him in accordance with the Copyright, Designs and Patents Act 1988. Library of Congress Cataloging-in-Publication Data [Métallurgie et mécanique du soudage English] Metallurgy and mechanics of welding : processes and industrial applications / Edited by Regis Blondeau. p. cm. Translation of Métallurgie et mécanique du soudage and Procédés et applications industrielles du soudage. Includes bibliographical references and index. ISBN 978-1-84821-038-7 1. Welding. I. Blondeau, Régis. II. Title: Procédés et applications industrielles du soudage. TS227.M385 2008 671.5'2--dc22 2008027554 British Library Cataloguing-in-Publication Data A CIP record for this book is available from the British Library ISBN: 978-1-84821-038-7 Printed and bound in Great Britain by CPI/Antony Rowe Ltd, Chippenham, Wiltshire.
Table of Contents
Preface . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . xiii Chapter 1. Traditional Welding Processes . . . . . . . . . . . . . . . . . . . . . . . 1 Guy MURRY and Dominique KAPLAN 1.1. Introduction. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.2. Conditions to create metallic bonding . . . . . . . . . . . . . . . . . . . 1.2.1. Activation of surfaces . . . . . . . . . . . . . . . . . . . . . . . . . . 1.2.2. Elimination of obstacles to bond creation. . . . . . . . . . . . . . . 1.2.3. How can we classify the various welding processes? . . . . . . . 1.3. Industrial welding processes . . . . . . . . . . . . . . . . . . . . . . . . . 1.3.1. Processes using local fusion of components without mechanical action . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.3.2. Processes using local fusion of components with mechanical action . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.3.3. Processes using heating without fusion but with mechanical action . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 1.3.4. Processes using mechanical action without heating. . . . . . . . . 1.4. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . .
. . . . . .
. . . . . .
1 1 2 3 4 5
. . . 5 . . 22 . . 27 . . 29 . . 30
Chapter 2. High Density Energy Beam Welding Processes: Electron Beam and Laser Beam . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 31 Abdelkrim CHEHAÏBOU and Jean-Claude GOUSSAIN 2.1. Welding properties using high density energy beams . 2.2. Laser beam welding . . . . . . . . . . . . . . . . . . . . . 2.2.1. History . . . . . . . . . . . . . . . . . . . . . . . . . . 2.2.2. Principle . . . . . . . . . . . . . . . . . . . . . . . . . 2.2.3. Various laser types . . . . . . . . . . . . . . . . . . . 2.2.4. Laser systems . . . . . . . . . . . . . . . . . . . . . . 2.2.5. Implementation of laser beam welding . . . . . . . 2.3. Electron beam welding . . . . . . . . . . . . . . . . . . . 2.3.1. History . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
. . . . . . . . .
31 33 33 34 35 41 48 52 52
vi
Metallurgy and Mechanics of Welding
2.3.2. Principle . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.3.3. Equipment . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.3.4. Design and preparation of the parts . . . . . . . . . . . . . . . . . . 2.4. Metallurgy of high density energy beam welding . . . . . . . . . . . . 2.4.1. Steels . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.4.2. Aluminum alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.4.3. Nickel-based alloys. . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.4.4. Titanium-based alloys . . . . . . . . . . . . . . . . . . . . . . . . . . 2.4.5. Zirconium-based alloys . . . . . . . . . . . . . . . . . . . . . . . . . 2.4.6. Copper-based alloys . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.5. Mechanical properties of welded joints . . . . . . . . . . . . . . . . . . 2.6. The quality of the assemblies . . . . . . . . . . . . . . . . . . . . . . . . 2.6.1. Weld defects . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.6.2. Weld inspection methods . . . . . . . . . . . . . . . . . . . . . . . . 2.6.3. Standardization and qualification of the welding operating mode 2.7. Economic aspects . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.7.1. Cost of an electron beam machine . . . . . . . . . . . . . . . . . . . 2.7.2. Cost of a laser beam machine. . . . . . . . . . . . . . . . . . . . . . 2.8. Safety . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.9. Examples of industrial applications. . . . . . . . . . . . . . . . . . . . . 2.9.1. Electron beam welding. . . . . . . . . . . . . . . . . . . . . . . . . . 2.9.2. Laser beam welding . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.10. Development prospects . . . . . . . . . . . . . . . . . . . . . . . . . . . 2.11. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . .
53 54 60 61 61 67 70 72 73 73 75 76 76 78 79 79 79 80 82 83 83 84 84 86
Chapter 3. Thermal, Metallurgical and Mechanical Phenomena in the Heat Affected Zone . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 89 Dominique KAPLAN and Guy MURRY 3.1. Thermal aspects related to welding . . . . . . . . . . . . . . . . . . . . . . . 3.1.1. Maximum temperature attained in the HAZ . . . . . . . . . . . . . . . 3.1.2. Cooling parameter in the HAZ . . . . . . . . . . . . . . . . . . . . . . . 3.2. Microstructural modifications in the HAZ: metallurgical consequences of the thermal cycles of welding . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.2.1. Transformations in the HAZ during heating . . . . . . . . . . . . . . . 3.2.2. Transformations in the HAZ during cooling . . . . . . . . . . . . . . . 3.2.3. Case of multipass welding. . . . . . . . . . . . . . . . . . . . . . . . . . 3.2.4. Cold cracking . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.2.5. Lamellar tearing. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.3. Influence of the thermal cycles on the mechanical properties of the HAZ . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.3.1. Modifications of the mechanical properties of hardness or traction in the HAZ. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 3.3.2. Toughness properties of the HAZ . . . . . . . . . . . . . . . . . . . . . 3.3.3. Residual stresses associated with welding . . . . . . . . . . . . . . . .
89 95 97 102 102 107 110 112 117 118 119 120 123
Table of Contents vii
3.3.4. Influence of residual stress relieving heat treatments in the HAZ . . 125 3.4. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 126 Chapter 4. Molten Metal . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 133 Christian BONNET 4.1. Metallurgical reminders . . . . . . . . . . . . . . . . . . . . . . . . . . 4.2. Molten metal . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.2.1. Thermal aspect . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.2.2. Chemical aspect. . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.2.3. Microstructures in ferritic steel welds: relationship with impact strength characteristics . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.3. Principal welding defects. . . . . . . . . . . . . . . . . . . . . . . . . . 4.3.1. Hot cracking . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.3.2. Cold cracking . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.3.3. Reheat cracking . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.3.4. Porosities . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 4.4. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . .
. . . .
. . . .
133 135 135 136
. . . . . . .
. . . . . . .
. . . . . . .
139 149 149 157 160 162 166
Chapter 5. Welding Products . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 169 Christian BONNET 5.1. Coated electrodes . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5.1.1. Constitution of coatings: consequences . . . . . . . . . . . . . . . 5.1.2. Basic electrodes and diffusible hydrogen . . . . . . . . . . . . . . 5.2. Fluxes for submerged arc welding . . . . . . . . . . . . . . . . . . . . 5.2.1. Fused fluxes and granular fluxes: advantages and disadvantages . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5.2.2. Roles of flux: metallurgical aspects . . . . . . . . . . . . . . . . . 5.3. Welding gases . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5.3.1. Welding processes under a gas flux with an infusible electrode 5.3.2. Welding processes under a gas flux with a fusible electrode . . 5.4. Cored wires . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5.4.1. Manufacturing processes . . . . . . . . . . . . . . . . . . . . . . . 5.4.2. Types of cored wires . . . . . . . . . . . . . . . . . . . . . . . . . . 5.4.3. The titanium/boron effect in relation to rutile cored wires . . . . 5.5. Choice of welding products . . . . . . . . . . . . . . . . . . . . . . . . 5.6. Welding products and the welder’s environment. . . . . . . . . . . . 5.6.1. Coated electrodes . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5.6.2. Gas mixtures for TIG welding . . . . . . . . . . . . . . . . . . . . 5.6.3. Gas mixtures for GMAW . . . . . . . . . . . . . . . . . . . . . . . 5.6.4. Cored wires . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 5.7. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . .
. . . .
. . . .
169 169 172 175
. . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . .
175 177 181 181 184 191 191 192 194 195 197 197 199 201 204 205
viii Metallurgy and Mechanics of Welding
Chapter 6. Fatigue Strength of Welded Joints . . . . . . . . . . . . . . . . . . . 207 Henri-Paul LIEURADE 6.1. Fatigue strength . . . . . . . . . . . . . . . . . . . . 6.1.1. Introduction . . . . . . . . . . . . . . . . . . . . 6.1.2. Fatigue failure of the principal welded joints 6.1.3. Concept of nominal stress . . . . . . . . . . . . 6.1.4. Factors in welded joint endurance . . . . . . . 6.2. Dimensioning of joints in mechanized welding . 6.2.1. Position of the problem . . . . . . . . . . . . . 6.2.2. General method (current regulations) . . . . . 6.2.3. Verification methods . . . . . . . . . . . . . . . 6.2.4. Geometric structural stress method . . . . . . 6.3. Bibliography . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
. . . . . . . . . . .
207 207 208 212 213 227 228 230 231 232 237
Chapter 7. Fracture Toughness of Welded Joints . . . . . . . . . . . . . . . . . 239 Marc BOUSSEAU 7.1. Ductile fracture and brittle fracture . . . . . . . . . . . . . . . . . . . . 7.2. Evaluation of fracture risks in metallic materials. . . . . . . . . . . . 7.2.1. Determination of the ductile-brittle transition temperature . . . 7.2.2. Determination of a fracture criterion in the elastic linear field . 7.2.3. Fracture criteria in the elasto-plastic field . . . . . . . . . . . . . 7.3. Evaluation of fracture risks in welded joints . . . . . . . . . . . . . . 7.3.1. Heterogenities of the weld bead . . . . . . . . . . . . . . . . . . . 7.3.2. Conditions of specimen taking . . . . . . . . . . . . . . . . . . . . 7.3.3. Determination of the ductile-brittle transition temperature . . . 7.3.4. Various methods of toughness evaluation . . . . . . . . . . . . . 7.4. Consequences of heterogenities on the evaluation of fracture risks . 7.4.1. Mismatching effects . . . . . . . . . . . . . . . . . . . . . . . . . . 7.4.2. Influence of the base material. . . . . . . . . . . . . . . . . . . . . 7.4.3. Influence of filler metals. . . . . . . . . . . . . . . . . . . . . . . . 7.4.4. Importance of welding conditions . . . . . . . . . . . . . . . . . . 7.4.5. Evaluation and taking account of residual stresses . . . . . . . . 7.5. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
239 241 241 245 249 253 253 255 256 258 262 263 266 269 269 270 273
Chapter 8. Welding of Steel Sheets, With and Without Surface Treatments . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 279 Gilles RIGAUT, Olivier DIERAERT, Pascal VERRIER and Joël CLAEYS 8.1. Spot welding . . . . . . . . . . . . . . . . . 8.1.1. Principle . . . . . . . . . . . . . . . . . 8.1.2. Tests of spot weldability. . . . . . . . 8.1.3. Spot weldability of thin steel sheets . 8.2. Seam welding . . . . . . . . . . . . . . . . 8.2.1. Mash seam welding . . . . . . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
. . . . . .
280 280 281 284 292 292
Table of Contents
8.2.2. Overlapping seam welding . . . . . . . . . . . . . . . . . . 8.2.3. Example applications studied or handled with customers 8.3. Laser welding of thin sheets . . . . . . . . . . . . . . . . . . . . 8.3.1. Principle of keyhole laser welding . . . . . . . . . . . . . . 8.3.2. Butt welding . . . . . . . . . . . . . . . . . . . . . . . . . . . 8.3.3. Lapped welding . . . . . . . . . . . . . . . . . . . . . . . . . 8.4. Arc welding. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 8.4.1. TIG welding . . . . . . . . . . . . . . . . . . . . . . . . . . . 8.4.2. MAG welding . . . . . . . . . . . . . . . . . . . . . . . . . . 8.5. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . .
. . . . . . . . . .
. . . . . . . . . .
. . . . . . . . . .
. . . . . . . . . .
. . . . . . . . . .
. . . . . . . . . .
ix
293 294 295 296 298 304 306 306 307 311
Chapter 9. Welding of Steel Mechanical Components . . . . . . . . . . . . . . 313 Yves DESALOS and Gérard PRADERE 9.1. Introduction. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9.2. Specificities of welded bonds in mechanical components . . . . . 9.2.1. Standard welding processes and general recommendations . . 9.2.2. Metallurgical defects in the molten zone and the HAZ . . . . . 9.2.3. Weldability limits for welding with and without remelting . . 9.3. Principal types of welding for mechanical components . . . . . . . 9.3.1. Electric arc welding and alternatives . . . . . . . . . . . . . . . 9.3.2. Welds with reduced HAZ using high density energy sources: laser beam, EB, plasma . . . . . . . . . . . . . . . . . . . . . . . . . . . 9.3.3. Friction welding. . . . . . . . . . . . . . . . . . . . . . . . . . . . 9.3.4. Butt welding by the Joule effect . . . . . . . . . . . . . . . . . . 9.3.5. Diffusion welding in the solid phase . . . . . . . . . . . . . . . 9.4. Specifications and quality control of the weldings for these components . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9.4.1. Weld quality specifications . . . . . . . . . . . . . . . . . . . . . 9.4.2. The quality assurance plan of the weld . . . . . . . . . . . . . . 9.5. Developments and trends. . . . . . . . . . . . . . . . . . . . . . . . . 9.5.1. Evolution of the context . . . . . . . . . . . . . . . . . . . . . . . 9.5.2. Favored processes . . . . . . . . . . . . . . . . . . . . . . . . . . 9.6. Conclusions. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 9.7. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
313 315 315 317 320 323 324
. . . .
. . . .
. . . .
. . . .
327 333 337 341
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
344 345 349 353 353 353 355 356
Chapter 10. Welding Steel Structures. . . . . . . . . . . . . . . . . . . . . . . . . 359 Jean-Pierre PESCATORE and Jean-Henri BORGEOT 10.1. Introduction . . . . . . . . . . . . . . . . . . . . . . . . . 10.1.1. History . . . . . . . . . . . . . . . . . . . . . . . . . 10.1.2. Applications . . . . . . . . . . . . . . . . . . . . . . 10.2. Steels for steel structures . . . . . . . . . . . . . . . . . 10.2.1. Grades and qualities . . . . . . . . . . . . . . . . . 10.2.2. Steels used . . . . . . . . . . . . . . . . . . . . . . . 10.3. Steel construction welding processes and techniques
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
359 359 361 362 362 363 364
x
Metallurgy and Mechanics of Welding
10.3.1. Table of the usual processes . . . . . . . . . . . . . . . . 10.3.2. Preliminary operation: tack weld . . . . . . . . . . . . . 10.3.3. Particular welding techniques . . . . . . . . . . . . . . . 10.3.4. Usual welding positions . . . . . . . . . . . . . . . . . . 10.3.5. Edge preparation . . . . . . . . . . . . . . . . . . . . . . 10.4. Welding distortion . . . . . . . . . . . . . . . . . . . . . . . . 10.4.1. Precautions in execution . . . . . . . . . . . . . . . . . . 10.4.2. Straightening . . . . . . . . . . . . . . . . . . . . . . . . . 10.5. Defects and their prevention . . . . . . . . . . . . . . . . . . 10.5.1. Cracks . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 10.5.2. Fracture . . . . . . . . . . . . . . . . . . . . . . . . . . . . 10.5.3. Other thermal and mechanical precautions . . . . . . . 10.6. Specificities of non-destructive testing of steel structures. 10.7. Developmental perspectives . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . .
. . . . . . . . . . . . . .
. . . . . . . . . . . . . .
. . . . . . . . . . . . . .
. . . . . . . . . . . . . .
. . . . . . . . . . . . . .
. . . . . . . . . . . . . .
. . . . . . . . . . . . . .
364 365 365 367 367 369 369 371 371 371 372 373 374 374
Chapter 11. Welding Heavy Components in the Nuclear Industry . . . . . . 375 François FAURE and Léon DUNAND-ROUX 11.1. General presentation of a PWR pressure vessel . . . . 11.2. Main materials used for manufacturing. . . . . . . . . 11.2.1. Principle of material choice – construction code. 11.2.2. Low alloyed steels for pressure vessels . . . . . . 11.2.3. Austenitic stainless steel circuits . . . . . . . . . . 11.2.4. Nickel alloy parts . . . . . . . . . . . . . . . . . . . 11.3. Welding of large low alloy steel components . . . . . 11.3.1. Properties aimed for . . . . . . . . . . . . . . . . . 11.3.2.Procedural description . . . . . . . . . . . . . . . . 11.3.3. Welding with coated electrodes . . . . . . . . . . 11.4. Cladding . . . . . . . . . . . . . . . . . . . . . . . . . . . 11.4.1. Cladding method . . . . . . . . . . . . . . . . . . . 11.4.2. Cladding inspection . . . . . . . . . . . . . . . . . 11.5. Welding of stainless steel circuits . . . . . . . . . . . . 11.6. Dissimilar metal interfaces . . . . . . . . . . . . . . . . 11.7. Welding of steam generator pipes . . . . . . . . . . . . 11.8. Conclusions . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . .
375 376 376 377 379 380 381 382 382 387 387 389 389 390 393 394 396
Chapter 12. Welding Stainless Steels . . . . . . . . . . . . . . . . . . . . . . . . . 397 Jean-Louis MOIRON 12.1. Definitions . . . . . . . . . . . . . . . . . . . 12.2. Principal stainless steel families . . . . . . . 12.3. Metallurgical structures . . . . . . . . . . . . 12.4. Constitution diagrams . . . . . . . . . . . . . 12.4.1. Introduction . . . . . . . . . . . . . . . . 12.4.2. Calculation of the equivalent formulae 12.4.3. Constitution diagrams . . . . . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
. . . . . . .
397 397 399 402 402 402 403
Table of Contents
12.5. Welding ferritic stainless steels . . . . . . . . . . . . . . . . . 12.5.1. Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . 12.5.2. Risks incurred in welding . . . . . . . . . . . . . . . . . . 12.5.3. Stabilization . . . . . . . . . . . . . . . . . . . . . . . . . . 12.5.4. Risks of embrittlement . . . . . . . . . . . . . . . . . . . . 12.5.5. Filler products . . . . . . . . . . . . . . . . . . . . . . . . . 12.5.6. Shielding gases . . . . . . . . . . . . . . . . . . . . . . . . 12.5.7. Summary: partial conclusion . . . . . . . . . . . . . . . . 12.6. Welding of martensitic stainless steels . . . . . . . . . . . . . 12.6.1. Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . 12.6.2. List of martensitic stainless steels . . . . . . . . . . . . . 12.6.3. Effect of the elements C, Cr and Ni on the J loop. . . . 12.6.4. Metallurgical weldability of martensitic stainless steels 12.6.5. Conclusion: partial summary . . . . . . . . . . . . . . . . 12.7. Welding of austenitic stainless steels . . . . . . . . . . . . . . 12.7.1. Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . 12.7.2. Risks incurred during welding . . . . . . . . . . . . . . . 12.7.3. Carbide precipitation . . . . . . . . . . . . . . . . . . . . . 12.7.4. Hot cracking . . . . . . . . . . . . . . . . . . . . . . . . . . 12.7.5. The sigma phase. . . . . . . . . . . . . . . . . . . . . . . . 12.7.6. Filler products . . . . . . . . . . . . . . . . . . . . . . . . . 12.7.7. Shielding gas. . . . . . . . . . . . . . . . . . . . . . . . . . 12.8. The welding of austeno-ferritic stainless steels (duplex) . . 12.8.1. Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . 12.8.2. Risks incurred in welding . . . . . . . . . . . . . . . . . . 12.8.3. Principal austeno-ferritic stainless steels . . . . . . . . . 12.8.4. Weldability of austeno-ferritic steels. . . . . . . . . . . . 12.8.5. Filler products . . . . . . . . . . . . . . . . . . . . . . . . . 12.8.6. Shielding gases . . . . . . . . . . . . . . . . . . . . . . . . 12.9. Heterogenous welding. . . . . . . . . . . . . . . . . . . . . . . 12.9.1. Reminder of definitions . . . . . . . . . . . . . . . . . . . 12.9.2. Treatment and forecast of heterogenous welds . . . . . . 12.10. Finishing of welds . . . . . . . . . . . . . . . . . . . . . . . . 12.11. Glossary . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 12.12. Bibliography. . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
xi
408 408 409 410 411 412 413 413 414 414 415 415 416 417 418 418 418 419 420 421 422 422 423 423 423 424 425 426 426 427 427 427 429 430 431
Chapter 13.Welding Aluminum Alloys . . . . . . . . . . . . . . . . . . . . . . . . 433 Michel COURBIÈRE 13.1. Metallurgy of welding. . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.1.1. Weldability of aluminum alloys (steels/aluminum comparison). 13.1.2. Filler metals . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.2. Welding techniques . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.2.1. Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.2.2. Arc welding processes (TIG-MIG). . . . . . . . . . . . . . . . . .
. . . . . .
. . . . . .
433 433 436 440 440 441
xii
Metallurgy and Mechanics of Welding
13.2.3. Electric resistance welding . . . . . . . . . . . . . . . . . . . . . 13.2.4. Flash welding . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.2.5. Friction welding and friction stir welding . . . . . . . . . . . . . 13.2.6. Electron beam welding . . . . . . . . . . . . . . . . . . . . . . . . 13.2.7. Laser welding . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.2.8. Other techniques. . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.3. Preparation and use of semi-finished aluminum welding products 13.3.1. Particularities of aluminum alloy surfaces . . . . . . . . . . . . 13.3.2. Storage . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.3.3. Surface preparation . . . . . . . . . . . . . . . . . . . . . . . . . . 13.3.4. Cleaning of the weld beads . . . . . . . . . . . . . . . . . . . . . 13.4. Deformations . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.4.1. Introduction . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.4.2. Steel/aluminum comparison (deformation due to heating) . . . 13.4.3. Shrinkage . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.4.4. Basic rules . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.5. Dimensioning of the welded structures . . . . . . . . . . . . . . . . . 13.5.1. Static . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.5.2. Fatigue dimensioning. . . . . . . . . . . . . . . . . . . . . . . . . 13.5.3. Rules governing the optimal use of welded structures . . . . . 13.6. Welding defects . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.7. Health and safety . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 13.8. Bibliography . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . .
. . . . . . . . . . . . . . . . . . . . . . .
447 448 449 451 452 453 454 454 455 455 456 457 457 458 461 461 464 464 467 467 468 471 471
Chapter 14. Standardization: Organization and Quality Control in Welding . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 473 Jean-Paul GOURMELON 14.1. Introduction . . . . . . . . . . . . . . . . . . . . . 14.2. Standards of general organization of quality . 14.2.1. Presentation . . . . . . . . . . . . . . . . . . 14.2.2. Principles . . . . . . . . . . . . . . . . . . . . 14.2.3. Analysis. . . . . . . . . . . . . . . . . . . . . 14.3. Standards for welding procedure qualification 14.4. Non-destructive testing standards . . . . . . . . 14.5. Conclusion . . . . . . . . . . . . . . . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
. . . . . . . .
473 474 474 475 475 479 484 487
List of Authors . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 489 Index . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . 491
Preface
Welding: The Permanent Bond Between Two Solid Bodies
What a long story welding is! Seeing the light of day at the end of the 19th century in the mind of scientists, it passed quickly into the hands of technicians, first of all with the oxyacetylene technique, then with arc welding and resistance welding techniques. Other processes (we will not quote them all in this introduction) then followed and the 20th century ended with laser welding which had its origins in the 1980s. However, it must be said that only since the 1950s has welding been the main means of assembly, as riveting was the most used method up to that point. In fact, after abandoning this method to some extent, scientists renewed their involvement in the 1930s. In France, at the time, Albert Portevin set out Les bases scientifiques de la soudure autogène and a higher education teaching programme began in 1931 at L’Institut de soudure. In the 1930s welding was implicated in bridge failures, notably in Germany and Belgium, then during World War II came the failure of Liberty ships constructed in great numbers thanks to the technique of welding. Other later catastrophic failures affected pressure vessels. It is in this context that in 1948 L’Institut international de la soudure (IIS/IIW) was founded. It met the need for international collaboration, in particular with regard to safety and research, expressed by different national bodies and by the whole welding world, from scientists to users. Today in 2008, the IIS/IIW holds its 61st annual meeting: 16 commissions, with sub-commissions and study groups, cover the whole field of welding, from design to performance and safety, including teaching and research. This demonstrates the importance of this collaboration and the richness of its contribution.
xiv
Metallurgy and Mechanics of Welding
Welding can be regarded, like the language of Aesop, as the best and worst of things. Indeed, it makes it possible to bond almost all materials, from metals to plastics, with continuity; however, this does not imply homogenity. The processes and hence possibilities are very numerous depending on the types of assemblies to be made, the properties required and evident economic constraints to be respected. At the same time welding can be regarded as the weak link of the majority of constructions as it is often called into question when problems arise. In the examples cited above (bridges, Liberty ships, pressure vessels) it is the welding that is called into question each time – often it must be added linked to a parent metal whose resistance to a sudden failure is insufficient. The phenomena that occur during welding are both numerous and complex. In particular, the influence of extremely rapid thermal cycles and at high temperature on the physical, metallurgical and mechanical properties of welded materials always requires a better understanding. In order to produce this work, the multiplicity of knowledge, scientific as well as technical, to be put in practice has led us to have recourse to a range of authors to share the task. The disadvantage is of course a certain disparity between the various chapters, as well as the risk of some repetitions. On the other hand, its richness is derived from this very fact as this work brings together the contributions of numerous French specialists well known in their specific field. It presents an entity as complete as possible on the knowledge available today on welding, without of course claiming to be exhaustive (for example, the welding of the plastics is outside its scope). In a first part of 7 chapters, which deals with metallurgy and mechanics of welding, Chapters 1 and 2 present all the processes of welding, from the traditional processes with and without filler, with and without mechanical action, to the recent processes with high energy, electron beam and laser. Chapter 3 deals with the whole of the thermal, metallurgical and mechanical phenomena, which occur in the heat affected zone (HAZ) of the base material. Here the transformation phases with all the consequences they have on the structures and their properties are presented, as well as the phenomena of cracking, in particular cold cracking, which is a recurring theme of this work. Chapter 4 is similar but deals with the question of molten metal in the weld, with other phenomena of cracking that are called into play.
Preface
xv
The different types of filler products are then dealt with in Chapter 5 depending on the process used. The progress made in the manufacture of these products in order to improve the properties of the weld and resistance to cracking is explained. Chapters 6 and 7 illustrate the problems of failure in service of welded constructions, the former dealing with resistance to fatigue, with solutions suggested both for materials and for the execution of the welds, the latter dealing with brittle failure, with, after setting out the methods of evaluation of the toughness and the evolution of the harmfulness of defects, proposals relating to the composition of the parent material, the quality of the filler metal and the importance of welding conditions. The second part, Chapters 8 to 14, focuses on the applications of welding for various materials and in various industries. First of all, Chapter 8 is devoted to the welding of thin sheets, both bare and coated, mainly used in the automotive market with the appropriate processes of welding. The importance of new steels with a very low percentage of carbon is underlined. The subject of Chapter 9 is the welding of steel mechanical components in the automotive industry, with less traditional processes calling upon a minimum of molten metal. The welding of steel structures is the subject of Chapter 10. The steels used and the techniques of welding with the precautions required in order to avoid defects are presented. Chapter 11 concerns the welding of pressure vessels. It deals with examples of large components such as pressurized water reactors (PWRs) in the French nuclear industry and analyzes the various processes of welding and coatings used according to the parts of the vessel. The majority of the preceding chapters refer to welding carbon and low-alloy steels, so Chapters 12 and 13 are devoted to other types of alloys. First of all, the welding of stainless steels is presented in detail, and for various families (martensitic, ferritic, austenitic and austeno-ferritic) with the concomitant problems of cracking and embrittlement, as well as the remedies and advice suggested according to the processes selected. Then, the welding of aluminum alloys is tackled with the various welding techniques used, the problems encountered and the rules to respect in order to obtain welds of good quality.
xvi
Metallurgy and Mechanics of Welding
Chapter 14 is devoted to standardization developments in welding dealing with the general organization of quality and standards for non-destructive testing. We extend our thanks to all those authors who have agreed to contribute to this work and especially those who work in the industry and who have been willing in their free time to contribute to this collection of the know-how and current research in the different fields of welding. Régis BLONDEAU
Chapter 1
Traditional Welding Processes
1.1. Introduction To avoid any misunderstandings, the definitions of the terms which appear in this text are those proposed in the document entitled “Terms and definitions used in welding and related techniques” published by the “Publications of Autogeneous Welding and the International Council of the French Language” [COL 96]. It has been specified in the preface to this book that welding makes it possible to reconstitute metallic continuity between the components to be assembled. This reconstitution involves the re-establishment of the interatomic metal bonding forces which requires at the same time a connection of the nodes of the crystal lattices and the absence of any foreign body likely to constitute a screen. This chapter will successively cover the physical conditions necessary to create the metallic bond and the industrial processes which make it possible to establish this bond. 1.2. Conditions to create metallic bonding Creating the metal bond consists, theoretically, of bringing the surfaces to be linked closer so that the surface atoms are at a distance of the order of the internodal distances of their own crystalline system.
Chapter written by Guy MURRY and Dominique KAPLAN.
2
Metallurgy and Mechanics of Welding
This operation, which would assume at the beginning that surfaces are chemically clean and in a specular state of polish, is not practically feasible. To mitigate this industrial impossibility, the surfaces to be joined will have to be activated with a view to eliminating the foreign bodies and elements likely to obstruct the creation of the bond. 1.2.1. Activation of surfaces The most effective surface activation is fusion which can simultaneously ensure their cleaning. The metallic bond is created by solidification. Different procedures can be employed: a) the two parts to be assembled undergo a surface fusion and thus contribute to the formation of a molten metal pool (possibly with the addition of a filler) which solidifies without mechanical action; b) the two parts to be assembled undergo a surface fusion but an external mechanical action expels the molten metal and creates the assembly by placing the surfaces in contact at the solidus temperature; c) the two parts to be assembled undergo a localized fusion and take part in the formation of a captive molten metal core which during its solidification is compacted by the action of an external effort of compression. The activation of surfaces can also be obtained by heating without fusion. In general it is then supplemented by a mechanical action which enables, moreover, cleaning and improvement in contact of the surfaces to be assembled. It is possible to distinguish between: a) the case where the heating and the cleaning of surfaces to be assembled are simultaneously carried out by mechanical friction (which implies the assembly of axisymmetric parts) and is followed, after stopping the latter, by a crushing (“forging”) by axial compression; and b) the case where the heating is carried out by external heating and the close contact is ensured by an effort perpendicular to the joint plane. Finally, activation can result from a mechanical action without total heating of the parts to be assembled. This mechanical action causes a plasticization of the outer layer of each surface and generates a very localized heating which finally allows the establishment of the metallic bond. This process simultaneously requires a relative displacement of the surfaces to be assembled, parallel to the mating plane, coupled with a compressive force perpendicular to this same plane. It is necessary to carry
Traditional Welding Processes
3
out a careful surface preparation and/or to make sure that relative displacements of the latter cause the rejection of the products which pollute them. 1.2.2. Elimination of obstacles to bond creation Obstacles to the creation of the metallic bond can be of various kinds: – geometrical surface irregularities, – pollution of the surface (oxides, grease, moisture, etc.), – chemical elements brought in by the surrounding air. Surface irregularities are likely to disrupt the creation of metallic bonds in all the cases where there is not surface fusion of the parts to be assembled. It will then be necessary to carry out a surface preparation by mechanical means (grinding, machining, etc.). All pollution of surfaces to be assembled will have to be eliminated by mechanical action (sanding, grinding) or by chemical means (solvents, scouring, drying, etc.). It is necessary to neutralize the possible effects of chemical elements brought in by the surrounding air. Welding operations generally being carried out in atmospheric conditions, it is especially oxygen, nitrogen and hydrogen (carried in the air’s humidity) which can be harmful. Oxygen can react with the elements volatilized by the arc and in this way contribute to the creation of welding fumes. Furthermore, it can especially dissolve in the molten metal and, during solidification, contribute to the formation of: – metallic oxides which constitute inclusions in solidified metal; – porosities in the molten metal due to the drop in solubility which accompanies cooling and solidification. This formation of porosities can be aggravated by a reaction developing with an element contained in the metal and leading to the formation of a gas compound (for example, formation and release of CO during steel welding without protection against the atmosphere). Protection against oxygen in the air can be ensured by the interposition of a neutral gas, a molten slag or by fixing in the form of oxides by the addition of oxygen hungry elements (silicon especially). In the vicinity of the molten metal, the surface of the parent metal raised to a high temperature can also react with oxygen and be covered with oxides, which is a further justification for using protective means, including at the back of the weld.
4
Metallurgy and Mechanics of Welding
Nitrogen can dissolve in the molten metal and contribute to: – either the formation of porosities in the molten metal due to the drop in solubility which accompanies cooling and solidification; – or the formation of metal nitrides which, according to the conditions in which they appear, constitute inclusions or precipitates more or less hardening and weakening in nature; – or for the part which remains in solid solution, a process of weakening by ageing. Protection against nitrogen can be ensured by interposing a neutral gas or a molten slag. Hydrogen dissolves in the molten metal and its concentration can reach high levels, even reaching saturation if precautions are not taken to limit its presence. Hydrogen, the solubility of which decreases when the temperature drops, can then contribute to the formation: – of porosities during solidification; – of cracks, in a solid state, when, oversaturated, it gathers in the form of gas molecules on the structural defects of a not very ductile metal. Protection against hydrogen primarily consists of limiting its introduction into the molten metal by lowering the atomic or ionic hydrogen content of the plasma arc. To do this it is necessary to minimize the water content of the surrounding air (no welding in a damp atmosphere), to interpose a gas low in hydrogen between the surrounding air and the arc, to eliminate compounds supplying water (hydroxides, condensation, greases, basic non-dried coatings, fluxes, etc.) and other sources of hydrogen (cellulose or rutile coatings and grease). 1.2.3. How can we classify the various welding processes? At this stage we are led to adopt a system of grading the welding processes according to the modes of action and means of protection against the atmosphere (see Table 1.1).
Traditional Welding Processes Activation
Complementary action
Protection
none
imperative
compression
not essential
heating
compression
possible
friction
compression
none
fusion
5
Table 1.1. Classing the welding processes according to modes of action and means of protection against the atmosphere
Actually, the various welding processes are above all classified according to more practical criteria, which are: – the energy source applied: flame, electric arc, plasma, Joule effect, spark, induction, friction, explosion, etc.; – the means of protecting the hot metal: gas or slag. 1.3. Industrial welding processes Industrial welding processes are set out here according to the criteria defined above, namely: – processes utilizing the fusion without mechanical action; – processes utilizing the fusion combined with mechanical action; – processes utilizing heating without fusion but with a mechanical action; – processes utilizing a mechanical action without heating. A classification akin to industrial practices will be presented at the end of this chapter. 1.3.1. Processes using local fusion of the parts without mechanical action For welding processes operating without voluntary mechanical action, the local fusion of the parts to be assembled can be described by distinguishing the mode of heating used and the means of protecting the molten metal against the chemical action of the surrounding air. Thus, it is possible to list: – flame or gas welding; – plasma welding;
6
Metallurgy and Mechanics of Welding
– arc welding; – vertical electroslag welding; – aluminothermic welding. It should be noted that, in all these processes, the molten metal weld pool is contained in a crucible formed by the shape of the parts to be assembled adjacent in the mating plane (sometimes the complete closure of the “crucible” is ensured by specific tools, e.g. slat, slides, mold). In this way a non-molten section of the parts, in the vicinity of the molten metal, is brought up to temperatures, according to its distance from the latter, between the temperature of the solidus of the metal and the initial temperature of the parts. The fraction of this volume (nearest to the molten metal), of which the structure and therefore the properties change because of this heating, is called the heat affected zone (HAZ). 1.3.1.1. Flame welding
Figure 1.1. Fusion of parent metals and filler metals obtained with a blowtorch
The fusion of the parent metals and the filler is obtained by heating with a blowtorch (Figure 1.1) which enables us, by combustion of a gas (acetylene generally, hydrogen, propane) with a comburent (which is generally oxygen), to have an effective flame (of a fuel rating, with acetylene, about 100 to 300 W/cm2 on a spot of heating [RYK 74], the diameter of which is about 5 to 10 cm). This flame comprises two zones, each with a specific role: – a cone at the immediate exit of the blowtorch nozzle whose surface constitutes the site of primary combustion (this, if acetylene is used, releases hydrogen and carbon monoxide). At the tip of the cone the temperature is very high (using acetylene, it exceeds 3,000°C) and the atmosphere is reducing; – a plume where combustion is completed. According to the adjustment of the consumption ratio, namely the ratio r = volume of oxygen to volume of acetylene, this plume can be oxidizing, neutral or reducing (and thus carburizing for steels). In welding a neutral flame is used corresponding to 1 d r d 1.2. The adjustment of blowtorch power is made by regulating the flow of acetylene which is governed by
Traditional Welding Processes
7
the nozzle diameter. Four nozzle sizes exist which give acetylene flows ranging from 10 by 63 l/h to 1,000 by 4,000 l/h. The flow of oxygen is regulated accordingly. This choice of acetylene flow takes account of the metal being welded, its thickness, the type of joint and the position of welding. It is possible to add a filler metal which is generally the same composition as the metal being welded and comes in the form of rods (from 1.6 to 5 mm in diameter). Thus, the blowtorch, from the temperatures reached, allows the fusion of metals and, by its atmosphere, ensures the molten metal is protected against any chemical reaction with gases in the surrounding air. However, with metals that are very sensitive to oxidation (aluminum, stainless steel, copper alloys) it is necessary to use a flux (spread out over the edges requiring welding or incorporated with the rod) to eliminate oxides formed on the surface. 1.3.1.2. Plasma welding
Figure 1.2. Plasma non-transferred arc welding
Fusion is carried out by heating using a plasma jet. This plasma is generated by the passage of a known plasma-producing gas (argon, with the possible addition of hydrogen or helium) in an electric arc created in the annular space formed between a coaxial nozzle and a refractory electrode (Figure 1.2). Generally, in DC, the refractory electrode is negative to avoid its destruction by the bombardment of electrons. The recombination in the jet of ionized species in the arc releases great energy and as a result generates a very significant rise in temperature which exceeds
8
Metallurgy and Mechanics of Welding
10,000°C. The specific power can vary from 500 to 10,000 W/cm2 on a heating spot [RYK 74] whose diameter varies from a few millimeters to a few centimeters). A peripheral tube ensures the distribution of an inert gas (generally argon or argon mixture + hydrogen) for the protection of the molten metal. This procedure, called a non-transferred arc or blown arc, is reserved for the assembly of relatively thin components.
Figure 1.3. Plasma transferred arc welding
The transfer of heat and therefore thermal efficiency is improved by striking the arc between the refractory electrode and the parts to be assembled. The arc is then maintained by a pilot arc which is created between the nozzle and the refractory electrode (Figure 1.3). The name given is plasma transferred arc welding. It is the procedure most commonly used in welding. It makes the assembly of thicker products possible (albeit with a variable limit depending on the nature of the base metal, but in the order of a centimeter), often by using the keyhole procedure; the plasma jet crosses the joint by pushing the weld pool backwards where solidification occurs (the faces to be welded can thus be straight edged). In this way complete penetration is ensured and regularized. The use of a support at the back of the weld is generally not necessary because the molten zone is quite narrow (although this does not obviate the need for gas protection at the back). However, this process is not suitable for carrying out a filler pass. It is generally employed in flat welding and sometimes in horizontal/vertical welding. A filler can be introduced in the form of wire. To increase the rate of deposit, it can be beneficial to use the hot-wire technique. However, the filler can also be introduced in the form of powder into the shielding gas jet (thus around the plasma jet).
Traditional Welding Processes
9
The synchronized generation of electric power pulses in the arc and in the plasma-producing gas flow makes it possible to weld in a vertical position. Such a procedure requires computerized control of all the parameters. 1.3.1.3. Arc welding The contribution of heat used to form the molten weld pool is assured here by an electric arc operating in DC or AC. The specific power can vary here from 103 to 105 W/cm2 on a heating spot [RYK 74] whose diameter varies from a few millimeters to a few centimeters. It must be possible for the arc to be generated easily and then remain stable. To facilitate its generation (which will allow us to avoid resorting to a too high starting voltage compared to the arc’s voltage in permanent mode) as well as to stabilize it, we have recourse to easily ionizable chemical elements which are introduced into the plasma arc. These elements can come from the fusible and volatile compounds included in the solid products which will form the slag or from gases applied to protect the molten metal. In addition, the power source must be adapted so that: – its non-load voltage is high enough to allow arc generation, – its normal operating voltage makes it possible to achieve arc lengths compatible with the technology employed, – its voltage in the event of the arc’s extinction is sufficient to allow the arc to be restored. The choice of polarity, in either AC or DC, must take account of the different phenomena which occur at the cathode and the anode. Indeed, electron emission takes place at the cathode and all the more so if the cathode is heated to a high temperature. However, if its heating is partially due to the direct Joule effect and the bombardment by the positive ions, it is above all due to the contribution of heat coming from the Joule effect which occurs in the cathode’s transition zone. This last point explains why the required current depends on the diameter of the cathode; the greater it is, the higher the current must be to maintain the cathode at a sufficient temperature. Electrons bombard the anode and thus cause significant heating, increased further by the Joule effect in the anode’s transition zone. If the arc uses DC, the choice of polarity depends especially on the process and the metal being welded, given that the anodic zone is heated more than the cathodic zone. The AC current supply makes it possible to alternate the phenomena at the two ends of the arc.
10
Metallurgy and Mechanics of Welding
When the filler comes from a consumable electrode, the transfer of this metal in the arc can be achieved in three different ways according to the electric mode of the arc. At high currents, the transfer takes place by pulverization, i.e. in the form of small droplets forcibly projected by the electric field towards the weld pool. At moderate currents the transfer takes place in the form of large droplets which, with little force applied to them, follow irregular trajectories before falling in the molten metal or, possibly in the form of projections to one side – which is generally a sign of a bad adjustment of the welding parameters. At the lowest currents the transfer takes place by short-circuit. The magnetodynamic effect is insufficient (the current is too low) to detach the droplet from the surface of the electrode; the droplet grows bigger to the point that it comes into contact with the molten metal. The shortcircuit then generates a current surge which detaches the droplet, which is incorporated in the molten metal. The products that ensure the protection of the molten metal can, according to the process, be: – fusible compounds which form a slag floating on top (and are likely to react chemically with it to refine its composition); – often inert gases (argon, helium or mixtures sometimes with the addition of hydrogen) with, sometimes, the addition of carbon dioxide (whose decomposition in the arc will give protective carbon monoxide and oxygen which will be fixed by elements introduced with the filler products). In this context, many processes have been developed that can be classified according to the conditions in which the arc is struck (between the two parts to be assembled or these components and an electrode) and that can also be distinguished according to the conditions in which the welding products are applied.
Traditional Welding Processes
11
Rotating
Figure 1.4. Rotating arc welding on pipes
a) The arc is struck between the two parts to be assembled Arc welding with pressure created with a magnetic field The arc is struck and moves between surfaces to be joined under the effect of a permanent magnetic field judiciously directed and controlled. After surface fusion, the parts to be joined are forced together (there is thus the formation of a seam). An alternative to this process is applied to tubular structures (Figure 1.4) using two coils which surround the tube and create two antagonistic magnetic fields. The resulting field is radial; it thus causes the rotation of the arc in the mating plane. This is rotating arc welding. Arc welding of studs The arc is formed between the end of the stud and the target zone of the support. After fusion of the stud end and creation of a molten pool on the surface of the support where the stud is to be fixed, the stud is plunged in the molten metal and maintained in position until solidification is complete. The power supply and stud displacement (contact, withdrawal for striking the arc, maintenance then lowering – Figure 1.5) are controlled automatically. The protection of the molten metal is generally ensured by the positioning of a refractory containment ring which ensures also the “molding” of the molten metal during its solidification. The power source
12
Metallurgy and Mechanics of Welding
comes from DC or capacitor discharge; the current intensity of the arc is adjusted according to the diameter of the stud. b) The arc is struck between a fusible electrode and the components to be assembled Generally, this procedure allows, with each operation, the deposit of a certain quantity of molten metal, a quantity which varies with the type of process and energy brought into play. It can prove insufficient to form a sufficient seam section between thick components; it is then necessary to carry out several operations i.e. several passes. Such a situation often requires an edge preparation to be performed, a preparation which ensures proper weld creation (access for the electrode, type of assembly, position, penetration, possible prevention of deformations, etc.). These preparations have shapes and dimensions which vary especially according to the nature of the base metal and the process employed. The principal varieties are: – straight edged (Figure 1.6a) for assemblies of limited thickness, possibly with spacing between the edges (distance increasing with the thickness). It may be necessary to carry out a pass on the reverse to ensure penetration but it is also possible to use a support at the back;
Figure 1.5. Stud arc welding
Traditional Welding Processes
13
– V-shaped chamfer (Figure 1.6b) or Y-shaped (Figure 1.6c) with heel and possible edge spacing. This type of preparation is not employed for thick components because it gives rise to considerable distortion; – X-shaped (Figure 1.6d) with heel and possibly edge spacing. This type of preparation requires access to both sides but limits distortion; – asymmetric U-shaped (Figure 1.6e) or, better symmetric (Figure 1.6f) if there is access to both sides (with heel and possibly edge spacing). This preparation makes it possible to reduce the quantity of molten metal necessary. Sometimes particular preparations such as half-V shaped, half-U shaped (known also as J), K-shaped, etc. are used. The processes which will be described are known as “semi-automatic” if the electrode or the torch is handled by the welder and “automatic” if the latter is positioned and guided by automated devices.
Figure 1.6. Edge preparations
14
Metallurgy and Mechanics of Welding
Figure 1.7. Coated electrode arc welding
Coated electrode arc welding The electrode consists of a metallic core (whose diameter varies from 1 to 10 mm and whose length can be up to 450 mm) which serves as the electrical conductor and supplies the filler metal, as well as an adhesive coating made up of products which contribute to the formation of a protective slag and others that volatilize in the arc plasma to stabilize it and, possibly, of metal particles which help form the molten weld pool (Figure 1.7). This coating can commonly be: – cellulosic: this creates little slag but its combustion releases CO2 and contributes to the enrichment of the molten metal caused by dissolved hydrogen; – rutile: the basic component is titanium oxide; it contributes to the desulphurization of the molten metal; the binding agents used release hydrogen; – basic (electrodes used in steel welding): the basic component is calcium carbonate; it releases little hydrogen but it is hygroscopic and so requires that the electrodes be correctly baked (300°C approximately) then protected (by maintaining them at around 100°C for example) before use. Rutilo-basic mixed coatings (better desulfurization) or rutilo-cellulose (good penetration) are also proposed as well as coatings containing metal powders to increase the quantity of metal added (high-output electrodes) or to introduce alloying elements.
Traditional Welding Processes
15
Core fusion slightly precedes that of the coating; it forms a crater which directs the transfer of the filler towards the molten metal. This transfer takes place in the form of large droplets (cellulosic or basic coatings) or by pulverization (rutile coatings). In many cases, the arc can be DC in origin (the polarity is then selected according to the nature of the base metal, the coating and the welding position) but it is sometimes possible to use an AC current (in particular for steel welding). The intensity of the current is selected according to the diameter of the electrode; it is generally recommended by the manufacturer.
Figure 1.8. Arc welding with powdered flux
Welding is in practice possible in all positions, each one requiring particular adjustments and appropriate preparation. Arc welding with powdered flux The electrode is a solid wire (approximately 2 to 10 mm in diameter) whose supply is guaranteed by an automatic device through a torch equipped with a contact tube ensuring the power supply. Upstream of the torch (compared to the direction of the welding process) a nozzle in which the arc will be struck distributes the powdered flux, part of which will constitute the protective slag, whereas the rest, covering the weld area with a layer of non-molten flux which slows down cooling, will be recovered later on. The arc is not visible, so consequently this imposes a precise piloting of the torch displacement.
16
Metallurgy and Mechanics of Welding
This process (Figure 1.8) makes it possible to weld with high currents and a high output. However, in general, dilution is significant, about 2/3 and it increases with the welding current. The arc is struck using DC when the welding intensity does not exceed 1,000 A; the polarity can be direct (the wire is negative) if deep penetration is required or inverse (the wire is positive) if, on the contrary, a high welding speed and a reduction in dilution is desired. With elevated currents it is sometimes easier to use AC, which makes it possible to decrease the effects of magnetic arc blow. The Joule effect along the length of wire electrode, between the contact tube and the arc, heats the filler metal (all the more depending on length and current) and facilitates its fusion, thus increasing the quantity of filler metal in the weld pool. Fluxes used are mixtures of mineral compounds (generally silicon manganese or silico-alumino-calcic compounds) delivered in the form of calibrated pellets. The two principal manufacturing processes give them different properties: – so-called molten fluxes are manufactured from minerals by fusion, molded and then crushed; they thus have a vitreous and/or crystallized structure and can be porous; – so-called agglomerated fluxes are manufactured starting from natural mineral products agglomerated or sintered (with a binder). These fluxes can adsorb or absorb water and so it is necessary to take precautions to avoid any addition of hydrogen. In general, the manufacturers of welding products combine flux and filler metal. Each combination often makes it possible to confer their own specific properties on the molten metal. This welding process, due to the method of flux application, enables only flat welding (and possibly at an angle with a special support). It allows straight edged butt welding with edge spacing up to significant thicknesses (depending on the base metal) but to weld very thick components it requires a preparation which account for the possibility of making a pass(es) on the reverse side: – no access: V-shaped preparation with heel, spacing and support at the back or tulip-shaped preparation or U-shaped with heel; – access: X-shaped with heel and spacing or K-shaped preparation with heel. Furthermore, welding can be accelerated by associating two (or more) welding heads each with its own power supply; the electrodes are generally placed in tandem at a distance of about 25 to 35 mm.
Traditional Welding Processes
17
Figure 1.9. MIG-MAG welding
Gas shielded arc welding with a solid fusible wire The electrode is a solid wire (from approximately 0.5 to 2.4 mm in diameter) whose supply is ensured by an automatic device through a torch equipped with a contact tube ensuring the connection to the power supply. This torch comprises an annular gas delivery which will ensure the protection of the molten metal. This gas can be of two types (Figure 1.9). It can be inert and the process is then known as MIG (metal inert gas) welding. It can be argon (pure or mixed with helium) which ensures good arc stability and gives a good penetration, or helium mixed with argon; the proportion of argon must be high enough to preserve arc stability. It can be active and the process is then known as MAG (metal active gas) welding. In this case it contains oxygen and, more often, CO2 mixed with neutral gases (argon mainly). The presence of oxygen (whether supplied or coming from the break up of CO2) brings a certain number of advantages: the arc is more stable, the weld pool more fluid, the transfer by pulverization can be established over a broader range of power supply conditions, the chamfers are filled better and voids less likely. However, the risk of loss of elements transported in the arc leads to the introduction of elements likely to combine with oxygen into the wire electrode. The power is generally supplied in DC and in inverse polarity (positive wire electrode) in order to increase the speed of wire fusion and to stabilize the mode of transfer, in the arc, of the molten metal. Two modes are mainly used: – the transfer by axial pulverization for the welding of thick products but limited to butt and flat angle welding or gutter welding; – the transfer by short-circuit which involves little energy and allows welding of thin products and all types of in situ welding.
18
Metallurgy and Mechanics of Welding
Certain modern equipment makes it possible to superimpose pulses over the basic current in order to cause the detachment of the drops at fixed frequency and thus to stabilize their size. It then becomes possible to control their transfer and to regulate their flow whatever the welding current. The term used is pulsed welding. Assemblies are made with all the preparation types already evoked but taking account of the need to allow sufficient access for the torch. This access can be facilitated by lengthening the wire electrode between the contact tube and the arc, with a resultant increase in the quantity of metal deposited in consequence of the heating by Joule effect in this length of wire and, generally, reduction in penetration. Welding can be carried out in all positions after adaptation of operational parameters.
Figure 1.10. Cored wire arc welding
Cored wire arc welding This process (Figure 1.10) is derived from gas shielded solid wire arc welding by a simple replacement of the solid wire with a flux cored wire (diameter from 1 to 4 mm). A cored wire consists of a tubular metal envelope filled with a powder (flux) whose composition and role are comparable with those of the coating on a coated electrode. According to the manufacturing process of cored wire, this can be closed (by drawing of a hollow cylindrical wire filled with flux) or formed by pleating or crimping and thus more or less sealed (but it can again comprise two parallel fillings containing flux and a metal filler powder). As the fluxes are hygroscopic and the metal sheath more or less sealed, it is necessary to take the same precautions for use as for coated electrodes. However, cored wires without slag (and thus containing
Traditional Welding Processes
19
metal powders) enable us, with an effective gas protection, to appreciably increase the welding speed and the quantity of metal added. As in MIG or MAG welding, the supply of the wire is guaranteed by an automatic device through a torch equipped with a contact tube ensuring the power connection. This torch makes an annular gas supply possible, which will ensure protection of the molten metal. This gas is generally reactive (CO2, possibly mixed with argon). The filled wire being more rigid than solid wire makes it possible to further increase the length of the wire electrode between the contact tube and the arc and thus to facilitate access (it is necessary to avoid over lengthening this distance so as not to separate the molten metal too much from the shielding gas). Assemblies are made with all the types of preparation already evoked by taking account of the improved accessibility given by the increased length of the wire electrode between the contact tube and the arc. This makes it possible to reduce the chamfer openings. In addition, the good penetration makes it possible to increase the height of the heels and to decrease the spacing between surfaces to be assembled. Welding is generally carried out on the horizontal and sometimes in other positions, in which case, a small diameter cored wire is used. Cored wires are also offered for welding without a shielding gas. Protection is then assured by both the slag (of which the limited quantity is not sufficient to ensure total protection) and by a dense atmosphere generated by specific products introduced into the flux. In addition, the metal sheath of the filled wire contains elements likely to decrease the harmful effects of an incomplete protection (deoxidizers and denitrifying agents). Finally the welding parameters are adjusted to reduce the length of the arc. These cored wires make it possible to decrease the size of the welding torch, to facilitate access and thus limit the preparation required.
Figure 1.11. TIG (tungsten inert gas) welding
20
Metallurgy and Mechanics of Welding
c) The arc is struck between a refractory electrode and the components to be assembled The non-consumable electrode consists of a tungsten tip (Figure 1.11) held in a torch equipped with an annular gas delivery which will ensure the protection of molten metal. This gas is neutral: argon (sometimes with the addition of hydrogen – up to approximately 30%) or helium. Argon gives good arc stability but helium ensures better thermal efficiency and thus deeper penetration. These considerations mean that argon-helium mixtures (about 80% Ar and 20% He) are often used. This process is most commonly called TIG (tungsten inert gas) welding. It can be necessary, depending on the base metal, to set up a gas protection on the reverse side using a gas which can be either identical or different from that supplying the torch (nitrogen-hydrogen). The electrode (0.5 to 10 mm in diameter) can be pure tungsten or tungsten with an addition of zirconium oxide (0.3-0.5%) or thorium (1-2%). These additions make it possible to increase the electrode emission capacity and thus to improve arc stability and help arc initiation. They also increase the electrode performance and thus the acceptable maximum current. The shape of the electrode point is a significant parameter of TIG welding. The electrode is often pointed in DC mode, and hemispherical in AC. The power supply is generally DC with direct polarity (negative electrode) so as not to subject the electrode to electron bombardment. In this way the energy impact is concentrated on the parts to be assembled and at the same time a narrow bead and good penetration are achieved. The arc can also be established by AC (with a suitable power source) when an electronic bombardment is desired to clean the parts to be assembled. Arc initiation is often assisted using a pilot arc. A filler can be introduced directly into the molten metal pool either in the form of rods or in the form of wire using a mechanized reel, allowing, if necessary, the pre-heating of the wire to improve the deposit rate. Assemblies are produced using all the preparation types already evoked above taking account on the one hand of the limitation of the volume of molten metal and, on the other hand, of the need for taking particular care (cleanliness, dimensional accuracy especially with regard to the spacing of the parts – it can be useful to set up a support on the reverse side). Welding can be carried out in all positions after adaptation of the operational parameters. An easier use of the TIG process and an increase in penetration can be obtained by applying a fine layer of a reactive flux to the surface of the edges to be assembled.
Traditional Welding Processes
21
The composition of this flux (often formed of oxides and/or halides) must be selected according to the nature of the base metal.
Figure 1.12. Vertical electroslag welding
Vertical electroslag welding This process consists of forming a molten metal bath in a vertical parallelepipedal mold formed by the two sections to be assembled and two watercooled copper shoes applied to the surface of the two parts (Figure 1.12). The continuous supply of molten metal due to the filler fusion (consumable wire electrode and possibly fusible wire guide) and the progressive solidification of the molten metal little by little consolidate the two parts. Above the molten weld pool, a bath of slag (thickness 40 to 60 mm) ensures its protection. The permanent heating is due to the Joule effect which develops partly in the electrode but especially in this molten mineral pool. Welding progresses vertically upwards. It begins with the striking of an arc between the wire electrode and an appendage which closes the bottom of the mold and on which a welding flux is deposited (which will form the slag). When the volume of molten metal is sufficient, the quantity of flux necessary to constitute the slag layer is introduced; the arc then ceases. It is generally preferable to set up, in the edge prolongation to be assembled, two blocks of the same
22
Metallurgy and Mechanics of Welding
composition as the base metal and of the same thickness. The weld’s end point will be after the molten metal has reached the level of these blocks so that the shrinkage at the end of solidification does not affect the weld per se (any surplus deposit thus created will be removed later on). According to the dimensions of the parts to be assembled, the side shoes can be moved upwards to follow the progression of welding. The heat affected zone is wide, because of the very significant heat generation. According to the thickness of the parts to be assembled several wire electrodes can be used simultaneously. To carry out welds of considerable height, a fusible wire guide plunged in the slag and melting simultaneously the wire electrode(s) can be employed; this fusible wire guide contributes to the molten metal weld pool. The term then employed is vertical electroslag welding with fusible wire guide. The procedure generally makes use of AC. This process allows butt welding and welding at an angle (by using adapted shoes) of work pieces whose thickness is generally not less than 40 mm. Aluminothermic welding In this process the welding is carried out by running a metal in fusion (filler) into a mold built around the two faces of the parts to be assembled, placed face to face, at a specified distance. These two faces are often pre-heated with a flame via holes provided in the mold. The molten metal is created on the spot by aluminothermy, i.e. exothermic reaction between oxides (of the metal filler) and powdered aluminum. This operation is carried out in a crucible placed at the top of the mold. As the molten filler is run in, the surface of the parts to be assembled melts, preceding solidification of the assembly. The protection of the molten metal is ensured by the slag which is formed during the aluminothermic reaction. Afterwards, it is necessary to remove the mold and grind the assembled parts, so as to eliminate any excess deposits. 1.3.2. Processes using local fusion of components with mechanical action The contribution of heat used to form the molten weld pool is assured here by the Joule effect of a high intensity alternating current which crosses the mating plane. It is the contact resistance between the two surfaces of the parts to be assembled which makes it possible to concentrate fusion in this plane. Several processes have been developed that we can classify according to the fate reserved for the molten metal; containment or expulsion. All require rather heavy and specific equipment.
Traditional Welding Processes
23
1.3.2.1. Resistance welding with containment of the molten metal This process combines the Joule effect and a mechanical pressure applied to the outside of the assembly, perpendicular to it and right where the molten metal zone is. This force has the aim of ensuring a good electrical contact between the parts to be assembled, thereby confining the molten metal in the zone where it is formed and applying pressure to it after its solidification in order to improve its compactness by avoiding shrinkage (an operation known as spot forging). Generally the electrodes carrying the current apply this effort. These considerations show that they are overlapping assemblies of products of limited thickness. The containment of the molten metal within the joint avoids any contact with the air; the problem of its protection thus does not arise. The effectiveness of this process is related to the localization of the zone heated by the Joule effect, which depends on the electric contact resistance between the parts; precautions must be taken so that, on the one hand, other resistances in series in the electric circuit are much lower and that, on the other hand, there is no possibility of the welding current being diverted to one or more parallel circuits. The piloting of the welding current as well as that of the compression force are handled by automatisms which can: – apply pressure before the passage of the current, to bring the two components into close contact and to ensure the electrical contact, – adjust the current intensity and limit its duration (in general, of a few periods to a few tens of periods i.e. durations which are calculated in tenths of a second), – adjust the pressure during the passage of the current to prevent the surfaces separating (due to dilation) and the consequent dispersion of the molten metal, – maintain or increase the effort to ensure the compactness of the volume of molten metal, – if required, run a reduced current as a post-heating. The electrodes are copper-based alloys. The addition of alloying elements (Cr, Zr, W, Cd, Co, Be, etc.) confers the necessary mechanical performance without overly affecting their electric conductivity and thermal conductivity. Their contact surface to be welded must be clean and uniform in shape.
24
Metallurgy and Mechanics of Welding
Figure 1.13. Resistance spot welding
In this way resistance spot welding, projection and roller seam welding can be carried out. Resistance spot welding In this process current supply and load application are carried out by cylindrical electrodes with tips in the shape of a truncated cone cooled by internal water circulation. Their contact surface is generally flat or slightly convex. They are installed on fixed machines or mobile tools; it is always desirable that the step-down current transformer is placed as close as possible to the welding zone. The volume of molten metal has an ovoid form and is called a spot weld. The welding is discontinuous and a seal cannot be guaranteed. The final load application generally causes an indentation on the two faces of the joint; it is possible to avoid on one of the two faces by replacing the electrode with a copper plate through which the welding current passes.
Figure 1.14. Projection welding
Traditional Welding Processes
25
It is possible, in certain cases, to carry out two spot welds simultaneously by coupling two transformers (double spot in series with push-pull assembly), or with only one transformer (provided that it is possible to control the currents). Resistance projection welding In this welding process (Figure 1.14), the passage of the current is localized by raised areas called projections created on one or both of the assembly surfaces. These bosses are stamped on thin flat sheets and machined in other cases. The supply of the current and the load application are applied, generally, using plates; during the heating and fusion the bosses collapse and the mobile plate must react very quickly to ensure the close contact of the parts to be assembled. If the power supply is powerful, it is possible and economic to weld several bosses simultaneously. The wear of the plates and deformation of the components are minimal. The geometry of the projections must be precisely controlled. Roller resistance welding In roller resistance welding (Figure 1.15), the electrodes are replaced by copper or copper alloy discs called rollers. These rollers are driven to ensure the progression of the components. Of course, they carry the electric current and apply the necessary load. The electric current, in general, is modulated as in spot welding but in a repetitive way and the welding consists of successive spots. It can be: – discontinuous if the successive spots do not overlap. It is possible to stop the roller rotation at each spot and to carry out spot compression, and the result is identical to that of spot welding. It is also possible to work uninterrupted but in this case without forging (the effort applied remains constant), – continuous if the various points overlap, i.e. if the formation of each point involves the partial remelting of the preceding spot. The welding then forms a perfect seal. It is possible, in roller welding, to carry out the seam welding of thin sheets using the force applied during welding; the extra thickness is then eradicated. It is necessary, to achieve this, that the overlap does not exceed one and a half times the thickness and that the sheets to be assembled are gripped very tightly.
26
Metallurgy and Mechanics of Welding
Figure 1.15. Roller resistance welding
1.3.2.2. Resistance welding with expulsion of the molten metal These processes combine the Joule effect with applied mechanical pressure, after heating, from outside of the assembly and perpendicular to it, over all its surface. This force has the aim of creating the bond by keeping in close contact the surfaces heated to their solidus temperature. A weld metal bulge is formed at the ends of the assembly, which must then be eliminated. As the heated zone is confined, the problem of its protection is not relevant. Within this framework two rather different processes are employed. Upset resistance butt welding The effort is applied in two stages: first of all for the cold joining of the parts in order to allow the passage of the current through the surfaces to be assembled, then, after passage of the current, to ensure the weld bond; an excess, or weld bead, is formed which must be eliminated. The Joule effect is limited to the contact zone between the two parts and the heating must bring them up to the forging temperature. This process is a large-scale consumer of energy and requires careful preparation of the faces to be assembled (which must be parallel and perpendicular to the effort applied). Therefore, flash welding is sometimes preferred. An alternative used for the longitudinal closure welding of cold formed sections utilizes high frequency (HF) induction heating. The HF current is applied by two contacts rubbing on the weld edges, above the intended weld, where they are still separate.
Traditional Welding Processes
27
Due to the skin effect, the current works its way along the edges to the contact point, where it generates heat (eventually to the point of fusion) and allows the bond to be formed with the pressure of two rollers. This process can be implemented each time it is possible to create an induced current which crosses the mating plane. Flash welding The parts are brought closer only after the current is supplied so that the current is first of all only transmitted by contact points created by the imperfections of the opposing surfaces; at these points the current density is very high. From the beginning of fusion the liquid part is expelled in the form of small incandescent particles; this is the flash. Gradually this flashing takes over the whole mating surface. Once this result is achieved the contact pressure is increased to drive out the molten metal and the impurities which it contains and to ensure the connection; the current is simultaneously shut off. An excess weld bead is formed in this last phase; it will have to be eliminated. A pre-heating of large section parts limits the electric output and the force required. It also decreases the loss of matter during flashing but increases the volume of the bead and the duration of the operation. This process does not require a careful preparation of the faces to be assembled; flashing alone is sufficient. In general, it is not necessary to protect the molten zone from oxidation in as much as the force is applied straight after the flashing. This process allows end to end welding of variously shaped components and sections (from just a few mm² to more than 1,000 cm²). 1.3.3. Processes using heating without fusion but with mechanical action Heating can be achieved from an external source (resistance or induction) or by mechanical action (friction). The applied forces must be carefully controlled. These processes thus require very specific equipment. Diffusion welding Diffusion welding is a process of solid state coalescence in which the parts to be assembled, put in contact under suitable pressure, are brought up to and maintained at a sufficiently high temperature (but very slightly lower than the melting point) to allow atom diffusion through the mating plane. This, helped by localized plastic deformations, can ensure metal continuity. The pressure can be: – perpendicular to the mating plane: it is then often recommended that to avoid macroscopic deformation, it does not exceed the limits of elasticity of the metal at the diffusion temperature,
28
Metallurgy and Mechanics of Welding
– isostatic: the pressure is in this case not limited and the resorption of porosities is greatly improved. The surfaces to be assembled must have undergone a careful preparation by fine polishing (to ensure the closest contact possible) and cleaning (to eliminate any pollution likely to obstruct the diffusion). It is possible to insert one or more nonfusible leaves (strip iron or deposit) between them. Precautions must be taken to avoid any hot reaction of these surfaces with the atmosphere (vacuum welding or in a neutral atmosphere). For a given preparation, the quality of the assembly depends on the pressure, the temperature and the duration of maintenance at temperature. It has been shown [LEF 92] that fast localized heating by induction under a judiciously modulated axial load (so as to be at any temperature equal to the corresponding limit of elasticity) makes it possible to achieve an assembly following a maintenance at a temperature whose duration varies, depending on its level, between 1 and 60 seconds. The heating conditions make it possible, in addition, to carry out a heat treatment within the framework of the thermal welding cycle. This procedure is applicable to many metals. Friction welding Friction welding is a process of butt welding under pressure which involves a rotation of the parts against each other (maximum circumferential speed of about 150 m/min) and the application of an axial load in order to generate, by friction, heat at the interface (only one part is put in rotation; it must be circular and its diameter, if solid, can vary from a few mm to 150 mm approximately). When the required temperature is reached, rotation is stopped and the axial load is simultaneously increased to ensure welding by forging. The rotating part is turned by a servo motor or a flywheel. In the first case movement stops due to disengaging and braking, in the second the stop follows the exhaustion of the flywheel’s kinetic energy (which was spun before the operation at a sufficient speed to ensure the required heating). The joint does not contain molten metal and this fact has two principal consequences: – the joint has good mechanical properties; – it is possible to weld different metals (iron and aluminum for example). An excess bead is formed at the periphery of the joint; it must be eliminated. The cleaning of the surfaces to be assembled is ensured by friction; this process thus
Traditional Welding Processes
29
requires neither careful preparation of the surfaces nor their protection in the course of the welding operation. If none of the two parts to be assembled can be rotated, it is possible to intercalate an adapter which can be rotated. A process which can be compared to friction welding is currently proposed under the name friction stir welding. It employs a non-consumable rotary tool, of suitable shape, which penetrates the mating plane; friction causes significant heating which lowers the elastic limit of the base metal. A significant plasticization develops and the tool movement (at a speed which would be approximately that used in arc welding) causes a flow of matter running from the front to the back of the tool, where it ensures the bond between the two parts to be assembled. The properties of such an assembly are interesting. Forge welding In this process the parts to be assembled are heated to a sufficient temperature then hammered to cause the connection by plastic deformation at the interface. Between the two faces to be assembled, it is necessary to employ a cleaning product (equivalent to a flux) which ensures the elimination of oxides by ejection during hammering. 1.3.4. Processes using mechanical action without heating Ultrasonic welding This is a process of lap welding under contact pressure, during which ultrasonic vibrations (20 to 100 kHz) are briefly applied so that the two faces to be assembled are set into motion against each other. A negligible volume of metal, on both sides of the mating plane, is thus raised (by friction) to the recrystallization temperature and ensures the bond as a result. The ultrasonic energy required is that much greater the thicker (generally not exceeding 2 mm) and harder the components are. It is possible to weld different metals. Explosive welding This welding process is used to produce assemblies by covering or cladding. The covering or cladding metal is violently projected against the base metal by the progressive detonation of an explosive layer distributed on its outside face. The shock wave, as it spreads, causes the ejection, in front of the contact zone, of a jet of metal which perfectly cleans the faces to be assembled and enables the creation of
30
Metallurgy and Mechanics of Welding
the bond. However, for this to occur, it is necessary that, before welding, a gap is established between the two faces which have been chemically cleaned beforehand. Their surface (from a few cm² to several m²) can be flat, cylindrical – tubes – or crooked. It is possible to assemble different metals. 1.4. Bibliography [COL 96] COLLECTIF, Termes et définitions utilisés en soudage et techniques connexes, Publications de la Soudure Autogène, 1996. [LEF 92] LEFRANCOIS P., KERGOAT M., CRIQUI B., HOURCADE M., “L’assemblage de l’acier en quelques secondes grâce au soudage-diffusion-dynamique à l’état solide: cas du 27CD4 soudé à 1050°C”, Mémoires scientifiques de la Revue de Métallurgie, January 1992. [RYK 74] RYKALINE N.N., “Les sources d’énergie utilisées en soudagé”, Soudage et techniques connexes, December 1974.
Chapter 2
High Density Energy Beam Welding Processes: Electron Beam and Laser Beam
Welding processes using high density energy beams result from the application, in the second half of the 20th century, of work conducted by physicists in the fields of x-rays and vacuum techniques for the process of electron beam welding and optronics for laser beam welding. The possibility of concentrating these beams on points having a very small surface area led engineers to use this property to melt materials to achieve welds or cuts. Compared to traditional arc welding processes, these two processes are characterized by a very high energy density at the impact point on the work piece. Rykaline [RYK 74] gave a representation comparing for several processes the heat flows at the center of the heat sources and the diameters of these sources. We can observe that the energy density measured at the focal point of a laser beam or an electron beam is 10,000 times higher than that reached in an oxy-fuel flame (see Figure 2.1). 2.1. Welding properties using high density energy beams These result from the dimension of the focal points (lower than a millimeter in general) used at the level of the parts to be welded. These properties are as follows: – single pass welding;
Chapter written by Abdelkrim CHEHAÏBOU and Jean-Claude GOUSSAIN.
32
Metallurgy and Mechanics of Welding
– welding without filler material when there is no gap between the parts to be joined; – welding of thin parts (tenths of millimeters) by heat conduction; – welding of very thick parts (tenths of millimeters) by the formation of a vapor capillary. In this last case, two modes of welding are observed: - complete penetration weld using a keyhole when the electron or photon beam passes through the whole thickness of the workpiece (see Figure 2.2), - partial penetration weld when the beam only melts part of the thickness of the workpiece (see Figure 2.2); – very narrow welds (molten zone and heat affected zone) because of the very high energy density; – welds inducing very low distortion, which makes these two processes a precision mechanical solution, since it thus becomes possible to weld machined parts or parts not requiring deformation correction after welding. Figure 2.3 illustrates the deformation (transverse and longitudinal shrinkage) obtained during the welding of a 15 mm thick sheet of martensitic steel by GTAW, plasma arc, GMAW and electron beam; – welds with gas protection (laser) or under vacuum (electron beam), which ensures a good protection against the oxidation of the molten zones and heat affected zones and makes it possible to weld materials sensitive to this phenomenon such as titanium and zirconium.
Figure 2.1. Rykaline’s diagram
High Density Energy Beam Welding Processes
33
Figure 2.2. Complete penetration and partial penetration welds (Institut de Soudure document)
Figure 2.3. Comparison of the transverse and longitudinal shrinkage of a butt welded martensitic stainless steel assembly (Institut de Soudure document)
2.2. Laser beam welding 2.2.1. History Einstein surely did not suspect the technological revolution to which his stimulated emission theory, established in 1917, would give rise. The technological adventure could only really start in 1954 when Professor Townes and his team developed the first stimulated emission amplifier and oscillator, which they baptized “MASER” (Microwave Amplifier by Stimulated Emission of Radiation). This discovery was followed by many others. In 1958, Schawlow and Townes demonstrated the theoretical possibility of producing coherent light by stimulated emission of radiation. The first laser source was a ruby laser produced by Maiman in 1960. It was very quickly followed by the development of the first gas laser by Javan (helium-neon laser). Many mediums were then studied and used for the
34
Metallurgy and Mechanics of Welding
manufacture of lasers: doped crystals, semiconductors, ionized gases, molecular gases, liquids, dyes. Laser is currently experiencing an extraordinary development. It is used in many spheres of activity. 2.2.2. Principle Laser is an acronym formed by the initial letters of Light Amplification by Stimulated Emission of Radiation. An atom can pass from a fundamental state E1 to excited state E2 by the absorption of a certain energy quantity (hȣ). This energy contribution can be mechanical or kinetic in origin. This atom will revert to its fundamental state by the restitution of this energy quantity, it is “the spontaneous emission” expressed by the following relation: hX
E2 E1
where h is Planck’s constant and ȣ the emerging photon frequency. These randomly emitted photons produce a light known as “incoherent”. There is no relationship of phase, direction and polarization between all these photons. If an incident photon causes a return to the fundamental state of the excited atom, there is “stimulated emission”. The two emerging photons are in phase, they have the same direction and same polarization as the incident photon: there is light amplification by stimulated emission of radiation. The excitation of the medium is called “pumping”. It allows the population inversion between excited and non-excited atoms. Pumping requires an external energy source which can be assured by electrical discharge or radio frequency in the case of gas lasers, and by lamps or laser diodes in the case of solid lasers. A laser source must thus be made up of three principal elements: – an active medium made up of particles (atoms, ions, molecules), – an energy source to carry out the pumping of the medium and thus to obtain the population inversion, – a resonator cavity made up of two mirrors ensuring photon oscillation. If one of the mirrors is partially reflective, it will allow some of the photons to escape which will constitute the coherent light beam.
High Density Energy Beam Welding Processes
35
The laser beam thus obtained will have certain characteristics of divergence, polarization and energy distribution which will define the quality of the laser beam. 2.2.3. Various laser types 2.2.3.1. CO2 laser sources Gas laser sources are most commonly used for working on materials. The active medium consists of a gas mixture containing helium (50%), nitrogen (40%) and CO2 (10%). Pumping is carried out by electrical discharge or more often by radio frequency. The excited nitrogen molecules transfer their excitation to the molecules of CO2. The radiation wavelength of 10.6 Pm thus obtained does not allow the transport of the beam by optical fiber. Only transport by mirrors, a less flexible system, is possible. In spite of the possibility of pulsing the beam, welding mainly uses CO2 in a continuous mode of operation. The electrical efficiency of such laser sources is lower than 10%. The search for increasingly powerful laser sources with a better beam quality and better efficiency have led to the development of various technologies. Those differ in the direction of gas circulation, the type of excitation and the shape of the cavity. We can distinguish five. Sealed laser sources These consist of a discharge tube containing the gas mixture. They are limited in power (d600 W) but deliver a very good quality beam. In the field of metallic materials, they are particularly well adapted to engraving and cutting thin sheets. However, their good beam quality also enables them to be used for the welding of thin strip iron. Advantages of such sources rest in their low cost and the possibility of installing them on mechanized systems. Slow axial flow laser sources These are the first CO2 laser sources to have been developed. The gas circulates slowly in the tubes in the axis of the laser beam (10 m/s). The excitation of gas is ensured by electrical discharge. These laser sources produce a very good quality beam but their power per unit of volume is limited to 0.5 W/cm3. The maximum power of these laser sources is low (d1,000 W). They can be used for cutting and welding thin materials. Fast axial flow laser sources The gas moves at high speed in the beam’s axis (t200 m/s) using pumps or turbines in the cavity made of glass tubes. The excited gas is then cooled by heat
36
Metallurgy and Mechanics of Welding
exchangers and progressively regenerated. The excitation can be obtained by electrical discharge but the most recent sources use radio frequency. This mode of excitation has several advantages: – more homogenous excitation, – the electrodes placed externally suffer less and their maintenance does not require the opening of the cavity, – greater flexibility in use. The power obtained per unit of gas volume can reach 2 to 3 W/cm3 for an excitation by electrical discharge and from 8 to 10 W/cm3 for excitation by radio frequency. Increasingly compact laser sources are obtained by reducing the cavity shape. Sources of 20 kW are proposed in today’s industrial market. These are the laser sources most commonly used today. They equip cutting and welding machines. Transverse flow laser sources The gas flow moves transversely across the axis of the laser beam thanks to one or more turbines. They do not use glass tubes. The cavity consists of a sealed metal chamber. The power per unit of gas volume is about 2 to 3 W/cm3. The maximum power reached is high (up to 45 kW). The laser beam obtained is of lower quality than for a fast axial flow laser. Such beams are mainly used for welding or surface treatments. So called SLAB laser sources The parallelepipedic cavity generates a rectangular beam configuration. The beam then passes into a spatial filter which makes it circular. The gas moves slowly in the cavity. The excitation of gas is carried out by radio frequency. The power available lies between 100 W and 6 kW. This technology makes it possible to obtain compact sources of a higher efficiency. Gas consumption is low and the beam obtained is of very good quality (close to Gaussian beam TEM00). 2.2.3.2. Neodymium YAG laser sources It is a solid-state laser whose active medium is yttrium aluminum garnet monocrystal doped with neodymium ions (Nd3+). The wavelength of this laser, 1.06 Pm, enables it to be transported by optical fiber. This low volume monocrystal (for example, a bar 150 mm in length and 9.52 mm diameter) is placed in a reflective cavity. The excitation of the medium is ensured by xenon lamps or laser diodes. The electrical efficiency of the laser depends on the pumping system, 1-3%
High Density Energy Beam Welding Processes
37
for a lamp pumped system and in the order of 10% for laser diodes. The cooling of the system is ensured by water circulation in the cavity. Two modes of Nd:YAG laser operation should be noted: pulsed and continuous. Pulsed YAG laser sources Pulsed YAG laser sources generally consist of a pumping module that delivers an average power ranging between 300 and 500 W. These YAG lasers can reach up to 2 kW on average by adding, in series, additional amplifying modules to this pumping module. The pulsed operation mode is ensured by flash lamps which produce with each impulse an optical response of a defined frequency and pulse length. The mode of operation for these lasers is schematized in Figure 2.4.
Figure 2.4. Pulsed YAG laser mode
The characteristics of a pulsed YAG laser are related to its peak power, which can reach 50 kW. The relations between the various laser parameters are as follows: – peak power: Pc E W ;
W
– average power: Pm
E u FW ;
– pulse duration: W(ms) ; – pulse energy: E(J) ; – pulse frequency: F(Hz) . High peak powers are reserved for drilling or cutting operations. For welding, the peak power must be limited and depends on the material and the thickness to be welded. They should not exceed 4 kW. The use of a high peak power will cause material spattering. For this reason, the average power of the sources intended for welding should be limited to 500 W. Sources of greater power will be used only for high pulse frequencies. The penetration depth will in any event be limited to 1.5 mm for a quality steel weld.
38
Metallurgy and Mechanics of Welding
Continuous YAG laser sources These were developed after pulsed YAG laser sources. The excitation of the medium is ensured by continuously lit xenon lamps. The average powers reached are higher than in the case of the pulsed YAG laser sources: 4 to 5 kW. The essential difference between the pulsed mode and the continuous mode lies in the peak power. In the case of the continuous mode, the peak power is equal to the average power.
Figure 2.5. Pumping chambers of a continuous lamp pumped rod YAG laser (4kW average beam power) (Trumpf document)
The current developments are mainly directed towards increasing the power of these sources and of the pumping system (see Figure 2.5). The power increase is obtained by the increase in the number of pumping chambers (resonators and amplifiers). In the case of a conventional laser source with cylindrical bars and lamp-pumping, the maximum number of pumping chambers currently put in series is eight. This limitation is mainly due to beam degradation. The beam quality of industrial continuous YAG lasers around 25 mm.mrad enables a laser beam of more than 4 kW to be carried in a 0.6 mm diameter optical fiber. The development of diode-pumped rod Nd:YAG laser sources in the year 2000 has offered scope for progress (see Figure 2.6). The system of pumping by laser diodes allows a better efficiency (t10%) and a clear improvement in beam quality (15 mm.mrad).
High Density Energy Beam Welding Processes
39
Figure 2.6. 4.4kW YAG laser source using laser diode-pumped rods (Rofin Baasel document)
The development of diode-pumped rod laser sources were a stage in the technological development of YAG laser sources but they have not been used industrially. They have encountered considerable technical problems linked to the reliability of the diode laser sources used for pumping. Today they have been replaced by new types of laser sources, diode-pumped disk laser sources and fiber laser sources. Disk laser sources For diode-pumped disk laser sources, the active medium consists of small sized YAG disks (see Figure 2.7). Laser sources up to 8 kW power beam are available for industry today, with a very high beam quality (0.8 mm.mrad) and high degree of efficiency. As opposed to the rod systems, the disk laser has no thermal lensing. This means that the beam quality is constant across the entire power range. Further developments of more powerful laser sources are expected in the near future (16 kW). The exceptional beam quality obtained using these laser sources allows the transport of up to 8 kW beam power in a 0.2 mm diameter optical fiber.
40
Metallurgy and Mechanics of Welding
Figure 2.7. Resonator diagram of a laser diode pumped disk source (Trumpf document)
Fiber laser sources This new laser source has recently been developed for industrial applications. It was initially developed for the telecommunications industry in the early 1990s. Its active gain medium is an optical fiber doped with a rare element like Ytterbium. This type of laser source can produce a very high power output (over 20 kW) with a very good beam quality. The efficiency attained is around 25%. 2.2.3.3. Semiconductor laser sources (or laser diodes) The stacking of a multitude of semiconductors makes it possible to obtain laser diode systems from a few tens of watts to several kilowatts. The wavelengths available are 0.808 and 0.940 Pm. The multiple beams emerging from these stacks are treated by sophisticated optical systems in order to be combined. The poor quality of beam produced is not conducive to optimal beam focalization. The rectangular and large-sized focal point generates power densities on the workpiece lower than 105 W/cm², which is insufficient for keyhole welding. These characteristics make it an excellent tool for the welding of synthetic materials, brazing, surface treatment or conduction welding. The particular advantage of this technology lies in its high energy efficiency (>25%), the compactness of the sources, the low operating costs (absence of lamps or lasing gas) and the low wavelengths (better absorption by metallic materials and possible transport by optical fiber). The development of optical systems allowing for a better focusing of the laser beam is keenly awaited and will revolutionize the use of these laser sources.
High Density Energy Beam Welding Processes
41
Figure 2.8. Diode laser source (Rofin Baasel document)
2.2.4. Laser systems 2.2.4.1. Laser beam transport The beam emitted by a laser source must be transported to the component to be welded with minimal losses. The transport and focusing systems used depend on the laser beam’s wavelength. Nd:YAG laser beams can be transported by optical fiber whereas the CO2 laser can only be transported by mirrors. In this case, the optical pathway must be confined and pressurized in order to avoid the mirror deterioration and the possible degradation of beam quality.
Figure 2.9. Insertion of a laser beam in an optical fiber; from >HAV 96@
The optical fiber must be as small in diameter as possible. The beam quality is then essential. Pulsed YAG laser beams averaging from 400 to 500 W in power can be inserted into a fiber 400 Pm in diameter, continuous YAG lasers pumped by 4 kW lamps use optical fibers 600 Pm in diameter and disk laser sources pumped by laser
42
Metallurgy and Mechanics of Welding
diodes benefit from a reduction in the optical fiber diameter (an 8 kW beam using a 200 Pm diameter optical fiber). The power losses are limited to less than 10% per optical fiber. The mirrors most commonly used for CO2 laser beam transport can be made out of bare copper, gilded copper or covered in molybdenum. Gilded copper is valued for its very low absorption properties but it is fragile and expensive. Bare copper also has low absorbance and is comparatively inexpensive, but tends to oxidize. Molybdenum covered copper is extremely resistant but its reflective properties are lower than the others. There is no precise rule for the choice of mirrors. It is however advisable to avoid using bare or gilded copper for focusing heads subjected to projections and welding fumes. The pressurized optical transport can consist of bare copper mirrors (less expensive), of gilded copper mirrors (good reflectivity) or of molybdenum covered mirrors (more resistant but more absorbent). 2.2.4.2. Focusing The laser beam must be focused on the workpiece in order to obtain the power density necessary to weld. YAG laser beams are generally focused using glass lenses. CO2 laser beams whose power is lower than or equal to 3 kW can be focused using selenium-zinc lenses or mirrors. Higher powered CO2 laser beams are generally focused using mirrors alone. These can be bare or gilded copper, molybdenum covered copper or solid molybdenum. Gilded copper is generally avoided for the construction of optical focusing heads because of its fragility. The dimensions of the focused beam depend on the beam wavelength, its quality and the focusing system used. The diameter of the focal point is related to these parameters by the following equation:
d
M 2(4Of / SD)
with: – d: diameter of the focal point, – M2: factor of beam quality, – O: wavelength, – F: focusing distance of the optical system, – D: diameter of the beam before focusing.
High Density Energy Beam Welding Processes
43
Figure 2.10. Laser beam focalization; from [HAV 96]
In the case of YAG lasers, the focal point diameter depends primarily on the optical fiber diameter, and on the collimation and focusing system (see Figure 2.11), which explains the importance of minimizing the optical fiber diameter:
Figure 2.11. YAG laser beam focalization; from [HAV 96]
Another important dimensional specification of the focal point is the field depth L. It is defined as being the zone in which the diameter of the beam increases no more than 5%. It can be expressed in the following way:
44
Metallurgy and Mechanics of Welding
While remaining within this tolerance of r5% of the focal point diameter, the variation in the resulting power density does not exceed 10%. We will see hereafter the importance of this criterion for the welding process. 2.2.4.3. Beam and workpiece displacement system There exist various mechanized beam and/or workpiece displacement systems. These systems are conceived according to the type of laser source used, the dimension of the parts to be welded and economic considerations. Contrary to the market of laser beam cutting, welding machines are often dedicated to an application. In order to reduce the costs, the manufacturers propose more and more machines by catalog or machines made up of standardized sub-assemblies.
Figure 2.12. Mixed three axis system (Balliu document)
For the simplest components, machines with fixed optics are used. The components are moved under the focused beam. Only the focusing optics are moved vertically to adjust the position of the focal point or to allow the loading and the unloading of the part. For this type of simple application, the optical pathway does not justify the use of optical fibers.
High Density Energy Beam Welding Processes
45
For more complex trajectories, we may have to use robotized systems with several axes of motion. There are two types: Cartesian robots or polyarticulated robots. Cartesian robots are mainly used for the mirror displacement in the case of CO2 lasers. They can incorporate up to five axes of motion. These precision mechanical systems, are expensive and require a rigorous optical pathway design (see Figures 2.12 and 2.13).
Figure 2.13. Five axis system with mobile optics (Trumpf document)
The development of high power continuous YAG laser sources and of beam transport by optical fibers has increased the use of polymorphic robots for welding operations. Their unquestionable advantage is the very competitive installation cost compared to the five axis Cartesian systems. The applications are currently mainly for the welding of automotive bodyshells (see Figure 2.14). These robots offer less positional precision than gantry robots, but this disadvantage can be compensated by the use of real-time trajectory monitoring systems.
46
Metallurgy and Mechanics of Welding
Figure 2.14. Six axis robot equipped with optical fibers for a YAG laser (Kuka document)
These robots can be equipped with a remote welding system (see Figure 2.15). This technology makes welding possible at a considerable distance from the workpiece. This remote process uses the latest high quality laser sources (disk laser and fiber laser sources). 2.2.4.4. Peripheral systems Peripheral systems are the devices that monitor the correct functioning of the laser system (power measurement, beam analysis, etc.), to supervise the welds being made (infrared thermography, plasma analysis) and facilitate robot operation (joint monitoring systems).
High Density Energy Beam Welding Processes
47
Figure 2.15. Six axis robot equipped with a remote laser welding system (Trumpf document)
Power measurement Laser sources are equipped with an internal system of power measurement. It gives an indication of the beam power emitted by the source. This power value does not take account of possible losses along the optical pathway. External measurement systems are available to measure the beam power at the component site. These systems do not allow the power measurement during welding, so they will be complementary to internal measurement systems, which can give an indication during the welding process. Beam analysis In the case of laser beam welding, the focused beam constitutes the welding tool, hence the importance of understanding its characteristics perfectly. Empirical methods allow an evaluation of the position and diameter of the focusing zone. The difficulty in using these methods increases with the power of the laser beam. Devices have been developed in order to determine laser beam characteristics in a precise way. The operating principle of these devices is based on taking away of part of the beam and analyzing it using photodiodes. On average, beams up to 20 kW with power densities 107 W/cm² can thus be analyzed. Weld monitoring One of the principal advantages of laser beam welding is its high speed. This advantage can quickly become a disadvantage if a defective weld is not detected in time. This can lead to the rejection of a great quantity of parts. It is thus necessary to monitor the welds on the production line in order to detect the defects as soon as possible. Several methods are employed.
48
Metallurgy and Mechanics of Welding
Infrared thermography – an infrared camera scans the back of the weld bead, very close to the weld pool. The anomalies noted in the temperature isotherms make it possible to highlight the formation of a welding defect. This control technique indicates the presence of an anomaly but does not give information about the quality of the weld. It can be used in addition to other monitoring techniques. This technique, which is difficult to control, is not very well suited for production line monitoring. Plasma analysis – this method consists of analyzing the emission of plasma and the weld pool. The sampling of data is carried out at the level of the laser/material interface by optical fibers or optical components located in the optical pathway. The sensors used are photodiodes whose fields of sensitivity can be located in the ultraviolet (emission of plasma), the visible range or infrared (emission of the weld pool). An analysis of the signal makes it possible to correlate the events detected with the appearance of weld defects. These devices make it possible to detect in real-time the formation of defects and to set off an alarm at a predetermined level. Control by closed loop is at the development stage. Seam tracking system Seam tracking, initially developed for conventional welding, has been adapted to laser welding. The laser triangulation technique makes it possible to carry out detection of the joint position in a reliable way for an environment where normal vision is disturbed (fumes, projections, highly emissive plasma). The majority of systems use the projection of a laser line which is compared with a computerized model [BOI 98]. Visualization by CCD camera is nowadays offered as a competitive alternative to laser triangulation. 2.2.5. Implementation of laser beam welding Laser/material interaction The laser beam is focused on the surface of the part so as to obtain a power density in the range of 5.105 and 5.106 W/cm². Figure 2.16 shows that a power density threshold exists for the creation of a vapor capillary or keyhole.
High Density Energy Beam Welding Processes
Figure 2.16. Penetration depth and absorption coefficient in relation to laser beam intensity; from [HER 86]
The threshold of the power density is a function of the following factors: – the nature of the material to be welded, – the laser beam wavelength, – the shielding gas, – the workpiece surface quality.
49
50
Metallurgy and Mechanics of Welding
The nature of the material plays a big role in the creation of the vapor capillary. Materials such as silver, gold, copper alloys and aluminum alloys are not easily weldable by laser beam because of their low absorption coefficients. Figure 2.17 shows that, because of their wavelengths, YAG laser beams and laser diode beams are absorbed better by metallic materials than a CO2 laser. We will see that the wavelength can be a selection criterion for the welding of materials with a low absorption coefficient.
Figure 2.17. Beam absorption in relation to wavelength; from [ROE 86]
The low absorption coefficient of a material can be compensated by a high power density. This high power density can be obtained by the use of a good quality laser beam, the choice of short focal length optics, the increase in laser power or, in the case of a YAG laser, the use of a small diameter optical fiber. The choice of assistant gas is also paramount. A good control of the gas supply and an appropriate choice in its composition have an important impact on the welding process and weld quality. Shielding gas The majority of the fusion welding processes (except the electron beam) require a shielding gas at the weld surface and if necessary at the back of the weld bead. In certain cases, a shielding gas covering can be used.
High Density Energy Beam Welding Processes
51
We can distinguish three zones to be protected: the weld pool, the surface of the weld just after solidification while still sufficiently hot to oxidize, and the root of the weld bead. For the protection of the weld pool and vapor capillary, we can use: – a coaxial nozzle, – a lateral nozzle, – a plasma blowing system. The coaxial and lateral nozzles transport gas at atmospheric pressure and at a low flow (15 to 30 l/min according to the power of the laser beam). They allow a good protection of the weld bead without disturbing the weld pool. The coaxial nozzle has the advantage of being usable for welding in all directions, which is not the case of the lateral nozzle. The use of a plasma jet is used in some particular cases. This consists of using a small diameter tube (d6 mm) tilted at an angle ranging between 35 and 45° in relation to the surface of part with a high gas output. The gas jet, directed a few millimeters above the surface of the part, blows the gas plasma. This system is little used, because it does not allow a good gas protection and tends to disturb the weld pool. The principal assistant gases used are the inert gases helium and argon or the active gas, that is, nitrogen. In the case of laser beam welding, gas protection does not only have the role of protecting the weld pool from contamination, it also takes part in the interaction between laser and material. The choice of gas thus depends on many factors: – ionizing potential of gases, – laser beam wavelength, – nature of the material to be welded. Gases subjected to a high density of power ionize more or less easily. Helium whose ionizing potential is high (24.46 eV) creates a not very intense and rather permeable plasma regardless of the laser beam’s wavelength. It can be used up to powers of 45 kW without particular problems. Argon and nitrogen, whose potential for ionization are lower (Ar: 15.68 eV and N2: 15.51 eV), create an intense plasma which hinders the interaction of beam and material. In the case of the CO2 laser beam, the use of these gases will be limited to powers d5 kW. From the perspective of welding performance, helium ensures the deepest weld penetration compared to nitrogen and argon and the narrowest weld beads. The addition of helium to argon makes it possible to limit the harmful influence of argon generated plasma. Commercial mixtures (helium/argon) are offered, especially for welding by laser beam. These mixtures can be used for powers up to 10 kW.
52
Metallurgy and Mechanics of Welding
In the case of the Nd:YAG laser, the choice of gas is not so important. The first data collected indicates that the use of argon or nitrogen with a Nd:YAG laser or fiber laser is possible with powers up to 10 kW. Argon and helium, being inert, can be used whatever the nature of the material to be welded, which is not the case with nitrogen. The latter can cause metallurgical transformations in the materials to be welded. It is not to be used for welding zirconium and titanium alloys, as it will form titanium nitrides and zirconium nitrides which will weaken the assemblies. Nitrogen can also cause an increase in the sensitivity to hot cracking of austenitic stainless steels because of its gammagene effect (it leads to the formation of austenite as well as primary austenite solidification). For these materials, its use will be subject to procedures that prevent hot cracking. However, because it is soluble in stainless steels, nitrogen could be used with some advantage to avoid the formation of porosities in the molten zone [BAR 98]. Its use for welding non-alloyed and slightly alloyed steels does not pose a particular problem if a high quality of welding is not required. 2.3. Electron beam welding 2.3.1. History [FRI 98] The earliest applications of the electron beam result from the work completed by K.-H. Steigerwald in Germany and by J.A. Stohr at the CEA (Atomic Energy Commission) in France. For the latter, this work was justified for the welding of combustible material casings made of zirconium alloy, a material very sensitive to oxidation and for which there did not exist, at that time, a suitable welding process. The production of an electron beam required vacuum conditions which naturally gave protection against oxidation. Thus, welding was made possible and the first EB welds were obtained using a focused electron beam produced by a Guinier cathode system. A patent was thus declared in 1956 and licenses granted to companies for the construction of machines, which appeared on the market in 1960. The first machines had low power electron beam guns (a few kilowatts), which limited the thicknesses that could be welded to approximately ten millimeters. Very quickly, the gun power that could be increased (30 kW in 1970), which made it possible to consider the welding of very thick parts (40 to 50 mm) encountered in boiler manufacturing or heavy engineering. During the 1980s, new applications were sought, with more than 1,000 machines being built in Western Europe between 1980 and the end of the 20th century.
High Density Energy Beam Welding Processes
53
2.3.2. Principle The process of EB welding uses the energy dissipated by electrons at the moment they strike the part to be welded. The electronic beam The electron is a particle characterized by its mass m = 9.1 u 10-31 kg and its negative electric charge e = 1.6 u 10-19 Coulomb. When this electron is placed in a space where an electric field E and a voltage V exists, it is subjected to a force F = eE. Under the action of this force, the electron moves with a speed v and will acquire, by ignoring the relativity effect, kinetic energy:
Ec
1 mv2 2
eV
If we consider n/t electrons emitted per unit of time, the power transported by the electron beam will be:
W
1 u n u mv2 2 t
ne u V t
I uV
with: – V: acceleration voltage of the electrons, – I: intensity of the beam. Specific power This is defined as the ratio between the power transported by the beam and the impact area of the beam on the parts to be welded. In welding, this specific power is a few tens of kW/mm-2. In fact, all the power is not transformed at the point of impact because of losses in the electron trajectory between the emission point and the point of impact on the part. The first losses are due to collisions with the atmospheric molecules; they are all the more significant the higher the air pressure is. The second losses are less important in quantity; they are due to re-emission phenomena, the most important of which is x-ray emission. The energy quantity thus dissipated is low (~ 1%) but the consequences are important from the perspective of safety.
54
Metallurgy and Mechanics of Welding
2.3.3. Equipment Three welding techniques appear according to the pressure value P close to the workpiece: – P > 10-5 mbar: secondary vacuum welding, – P ~ 10-2 mbar: primary vacuum welding, – P ~ 1,000 mbar: welding without vacuum. The equipment used is obviously different but they all include: – an electron beam gun with its viewing system, – a welding chamber containing the parts to be welded and sometimes the electron gun. This enclosure also contains the displacement systems for the parts and the gun, – a pumping unit to obtain a reduced pressure into the gun and the chamber, – a power supply and numerically controlled command and control circuits. The electron gun Figure 2.18 illustrates the principles of a triode electron gun, which include: – a cathode made of a very emissive material: tungsten, tantalum or lanthium hexaboride. This cathode is heated in vacuum conditions, either directly by an electric current (direct heated electron gun), or indirectly by a primary electron beam resulting from a heated filament (indirect heated electron gun); – a non-magnetic Wehnelt surrounding the cathode and acting, on the one hand, on the shape of the equipotential surfaces and thus on the shape of the beam (the electrons move perpendicularly to these surfaces) and, on the other hand, on the electron acceleration where this plays the part of a grid in a triode;
High Density Energy Beam Welding Processes
55
Figure 2.18. Principle of a triode electron gun (Institut de Soudage document)
– a copper anode carrying a positive charge compared to the Wehnelt creating the electric field to accelerate the electrons. This anode is bored in its center with a channel which allows the electron beam to pass through. This converges immediately at the exit of the anode then diverges under the effect of mutually repulsive electrons as they move apart; – a magnetic focusing coil with windings in the same axis of symmetry as the gun. It reconcentrates the divergent beam and concentrates it on a small point (about a millimeter in diameter); – a set of magnetic deflection coils enabling the beam to move in relation to its axis (side sweepings, circular movement, etc.); – a system for accurately positioning the beam on the joint by an optical viewing system or a television camera system. According to the electrode geometry and in particular of those of the anode and Wehnelt, the maximum current available I will be determined according to the acceleration voltage V by a characteristic of the gun called perveance p and expressed as:
56
Metallurgy and Mechanics of Welding
I
p uV3/ 2
The gun powers vary according to the thicknesses which need to be welded. They range from 5 to 100 kW but most of the installations are equipped with guns that have a power ranging between 10 and 30 kW. With regard to the acceleration voltages, here those lie between 45 kV and 150 or even 300 kV, depending on the technologies chosen by the manufacturers and the power required from the gun. The welding enclosure and displacement mechanisms The enclosure (vacuum chamber) contains the parts to be welded with their tools and their workpiece displacement. It can also contain the electron gun with its displacement system with one or more axes. Generally, this enclosure must be of a low volume compatible with that of the parts to be welded, but it should be understood that too large a volume involves a longer pumping time, which has a detrimental effect on the equipment productivity.
Figure 2.19. 6 kW EBW machine; dimensions 0.6 m u 0.6 m u 0.9 m (Techméta document)
In addition, these enclosures must be designed to resist atmospheric pressure without any deformation and their internal sides walls must be clean in order to limit the effects of gas adsorption and thus reduce the pumping time.
High Density Energy Beam Welding Processes
57
The enclosure volumes used industrially vary between 0.5 m3 and more than 1,000 m3 (see Figures 2.19 and 2.20).
Figure 2.20. 50 kW EBW machine with internal gun; dimensions 8 m u 5 m u 5 m (Techméta document)
In order to avoid building large-scale enclosures, it is desirable to create the vacuum locally, where the weld is to be made. This solution was adopted between 1970 and 1980 for various applications, including the welding of connecting pipes on boilers or tubes on tubular exchanger plates. Although tempting a priori, this solution has effectively been abandoned, because equipment with localized vacuum chambers was very expensive due to its application to only one type of part, and it did not offer great flexibility in use. The systems for positioning and moving the parts are tables with one or two axes or turning gears for the welding of rotating parts. These mechanical axes are controlled numerically.
58
Metallurgy and Mechanics of Welding
Vacuum creation systems For the machines in primary vacuum, the pumping unit consists of standard mechanical pumps (rotary vane pumps or Roots booster pumps). For those working in secondary vacuum, one or more oil diffusion pumps or turbomolecular pumps are added. The pumping unit’s delivery is a function of the enclosure volume to be pumped, the pumping time and degasification related to the nature and the thickness of material being welded. This last criterion is particularly important when welding very thick parts. This pumping delivery can reach levels from 2,000 to 5,000 m3.h-1 for mechanical pumps and from 10,000 to 20,000 l.s-1 for oil or turbomolecular pumps. Non-vacuum machines or under reduced pressure [POW 00] The first industrial non-vacuum EB welding machine was used in the USA automotive industry towards the end of the 1960s. The essential characteristic of this type of equipment lies in the absence of a vacuum chamber, which is very important for mass production, e.g. automotive components like transmission components, torque converters and exhaust systems. Counterbalancing this advantage is the disadvantage of having to use a very high acceleration voltage (150 kV) in order to obtain a sufficiently powerful beam on the work piece, in spite of passing through a gaseous atmosphere of only a few millimeters. This high voltage generates strong X-ray emissions and it is thus necessary, in order to protect the operators working on the machine, to create an enclosure ensuring containment of this radiation. Unlike in the USA, this type of process was little used in Europe. However, since 1990, significant developments have led to new equipment which functions at atmospheric pressure or under reduced pressure (200 ppm. Alloys whose Cr/Ni equivalent is between 1.58 and 1.70 are in a transitory zone where hot cracking depends on impurity content.
Figure 2.24. Austenitic stainless steel pulsed YAG laser bead on plates; from [CHE 93a]. X2CrNi18-09 Cr/Ni eq. = 1.75% (S + P + B) = 0.0475% (figure on left) X2CrNiMo17-12-2 Cr/Ni eq. = 1.57% (S + P + B) =0.0481% (middle) X2CrNiMo17-12-2 Cr/Ni eq. = 1.523% (S + P + B) =0.0106% (figure on right)
This work showed that external factors, such as the use of nitrogen (gammagene) as a shielding gas, can contribute significantly to the formation of cracks (see Figure 2.25). Ferritic stainless steels The main issues encountered during the welding of ferritic stainless steels are grain enlargement and nitride and chromium carbide precipitation which can cause intergranular corrosion. These phenomena are particularly prevalent during the use of welding processes using high linear energy. The high density energy beam welding processes, with low heating and high cooling rate, limit these phenomena and improve the welded joint’s mechanical strength in a significant way.
High Density Energy Beam Welding Processes
65
Figure 2.25. Comparison of beads on plates carried out with various shielding gases (from [CHE 93]). Bead on plate with helium (figure on left). Bead on plate with nitrogen (figure on right)
Martensitic stainless steels Martensitic stainless steels can be sensitive to the cold cracking phenomenon. The factors which give rise to cold cracking are: – high percentage of carbon (>0.3%), – stresses caused by the welding process or unsuitable joint design, – high cooling rates, – the presence of hydrogen in solution.
66
Metallurgy and Mechanics of Welding
Figure 2.26. CO2 laser beam lap weld of X2CrMoTi 18-2 ferritic stainless steel (Institut de Soudure document)
Various arrangements make it possible to limit or avoid the cold cracking of these steels: – the use of an austenitic filler wire, – pre-heating and post-heating, – avoidance of hydrogen introduction. The high density energy beam welding processes have great advantages compared with conventional processes. Having no contact with the part to be welded, they limit hydrogen contamination, and with the molten zone being very narrow, the stresses caused by shrinkage during solidification are significantly reduced. Certain steels considered unweldable by arc processes have been welded without filler wire and pre-heating. Precipitation hardening martensitic stainless steels lose their mechanical properties after welding if they are welded in an age hardened state. It is appropriate, if the design of the parts allows it, to weld in a hyperquenched state and to carry out the ageing treatment after welding. Austenoferritic stainless steels (duplex or super-duplex) These steels owe their good mechanical characteristics and their good corrosion resistance to their microstructure made up of 50% of austenite and 50% of ferrite. The high cooling rate induced by welding causes an imbalance between ferrite and austenite. The high cooling rate generated by the high density energy beam welding processes involve the formation of an almost entirely ferritic structure in the molten zone. The reduction in welding speeds and/or the introduction of nitrogen as a
High Density Energy Beam Welding Processes
67
shielding gas increases the austenite content. Unfortunately, these techniques do not suffice to obtain a duplex structure (see Figure 2.27). The high density energy beam processes will be usable only whenever the corrosion requirements are not at maximum.
Figure 2.27. CO2 laser butt welded joint of 3 mm thick austenoferritic stainless steel; X2CrNiMoN22-5-3 (Institut de Soudure document)
2.4.2. Aluminum alloys Operative weldability The main issues of operative weldability for aluminum alloys relate to the presence of the refractory oxide layer and their high conductivity. The oxide layer requires the surface cleaning of the parts before welding, whatever the welding process used. The laser welding of aluminum alloys is made more difficult because of their low absorption coefficient. In this case, a YAG laser has a slight advantage compared to the CO2 laser because of its lower wavelength, which allows a better radiation absorption. Electron beam welding has advantages for the welding of these alloys because it does not have the absorption problem of laser beams, while the weldable thicknesses are high (see Figure 2.28) and the weld beads are narrow. The thermal welding cycle is sufficiently short, which limits the problems caused by aluminum’s high thermal conductivity.
68
Metallurgy and Mechanics of Welding
Figure 2.28. Electron beam weld of aluminum alloy 5754 (Institut de Soudure document)
Metallurgical weldability In a similar way to austenitic stainless steels, aluminum alloys react differently to the pulsed or continuous welding mode. The solidification speed obtained during pulsed YAG laser beam welding causes the systematic appearance of hot cracking. Only pure aluminum and the 4000 series aluminum (Al, Si) can be welded without hot cracking. The 5000 (Al, Mg) and 6000 (Al, Mg, Si) series aluminum alloys can be welded either in a heterogenous assembly with the 4047 aluminum alloy (or 4043) or by using this alloy as filler wire. Continuous mode welding processes cause fewer hot cracking problems. They make it possible to weld 3000, 4000, 5000 and 6000 series aluminum alloys under good conditions. The 6000 series can however present hot cracking phenomena for high welding speeds. For laser welding, the use of 4047 (or 4043) filler wire can avoid this hot cracking phenomenon. However, this can give rise to a liquation phenomenon.
High Density Energy Beam Welding Processes
69
Figure 2.29. CO2 laser beam weld of 5 mm thick aluminum alloy 6013; from [CHE 98]
In the case of 2000 series aluminum alloys, only alloy 2219 is truly weldable. Aluminum alloy 2024 can be welded with caution at a low welding speed.
Figure 2.30. CO2 laser beam weld of 5 mm thick aluminum alloy 2219; from [CHE 98]
The 7000 series alloys must be welded with precaution, because they have a strong tendency to hot cracking. Aluminum alloy 7020 can be welded by electron beam (see Figure 2.31). It is advisable in this case to take account of the restraint effects caused by the design of parts.
70
Metallurgy and Mechanics of Welding
Figure 2.31. 2 mm penetration depth in a aluminum alloy 7020 welded by electron beam (Institut de Soudure document)
2.4.3. Nickel-based alloys Operative weldability Like stainless steels, nickel-based alloys do not pose any particular operative weldability problem. It is however necessary in the case of laser welding to provide an adequate shielding gas using a gas carriage. Metallurgical weldability Nickel-based alloys can be classified into two big groups: – non-heat-treated alloys: these offer good corrosion resistance. Such alloys offer, in general, good weldability; – precipitation hardening alloys: these are used for their good mechanical properties at high temperature. They are sensitive to hot cracking. A post-weld heat treatment is often necessary (see Figure 2.32).
High Density Energy Beam Welding Processes
Figure 2.32. CO2 laser beam weld of 6 mm thick Inconel 718 (Institut de Soudure document)
Figure 2.33. Electron beam weld of 100 mm thick titanium alloy TA5E (Institut de Soudure document)
71
72
Metallurgy and Mechanics of Welding
2.4.4. Titanium-based alloys Operative weldability Titanium alloys respond well to laser beam or electron beam welding. They have a good fluidity which helps the formation of an aesthetic weld bead. The use of excessive energy densities will cause surface defects like undercuts (see Figure 2.33).
Figure 2.34. CO2 laser beam weld of 6 mm thick alloy TA6V (Institut de Soudure document)
They have, however, a great sensitivity to oxygen and nitrogen. An effective gas shield is required during welding. Contamination by oxygen and nitrogen entails particle formation, which increases mechanical resistance to the detriment of toughness and thus will weaken the structure. For this reason the vacuum electron beam is an excellent alternative. Metallurgical weldability Certain alloys are sensitive to grain enlargement during welding. As for ferritic stainless steels, high density energy beam processes significantly limit this phenomenon. The weld beads obtained by laser or electron beams have a better ductility than those obtained by arc welding. The alloys usually employed are not very sensitive to hot cracking.
High Density Energy Beam Welding Processes
73
2.4.5. Zirconium-based alloys Operative weldability The behavior of zirconium alloys is similar to titanium-based alloys. They can be easily contaminated by ambient air. Oxidation starts at 400 to 500°C. Surface and back gas shielding must be guaranteed. The electron beam is the favored process for these alloys. A pulsed YAG laser beam can be used because of the limited heating effect.
Figure 2.35. Pulsed YAG laser weld of 1 mm thick zirconium alloy Zy4 (Institut de Soudure document)
Metallurgical weldability Certain alloys are commonly used because of their good metallurgical weldability. This is the case for Zircaloy in the manufacture of casings for the nuclear industry. Zirconium alloys are sensitive to grain enlargement, hence the value in using high density energy processes. 2.4.6. Copper-based alloys Operative weldability The great reflectivity and high thermal conductivity of copper alloys are major disadvantages for laser beam welding. It acts just as a mirror. The pulsed YAG laser
74
Metallurgy and Mechanics of Welding
beam, thanks to its high density of energy, can sometimes be used for welding very thin parts. On the other hand, the electron beam presents many advantages. It makes it possible to weld thick sections without pre-heating. The weld beads obtained are narrow.
Figure 2.36. Electron beam welding of a copper part (Institut de Soudure document)
Metallurgical weldability Pure copper exists in different levels of purity: – Cu-a1: 99.90% pure, contains up to 0.1% of oxygen, – Cu-b: 99.90% deoxidized with phosphorus, – Cu-c1: 99.94% pure, – Cu-c2: 99.96% pure. Copper must be welded in deoxidized types Cu-c1 or Cu-c2. Whatever the origin of the oxide, when it occurs as intergranular precipitates, it weakens the weld and its surroundings. It can also cause the formation of porosities. The main copper alloys have a good metallurgical electron beam weldability. A hot cracking phenomenon is possible for certain alloys such as cupro-aluminums, cupro-berylliums and certain brasses. It is absolutely essential to avoid the presence of lead (alloys with improved workability) which increases the tendency to hot cracking.
High Density Energy Beam Welding Processes
75
2.5. Mechanical properties of welded joints High density energy beam welds have specific characteristics such as single pass welding, a narrow molten zone and the absence of filler wire. These characteristics will have an influence on the traditional mechanical properties. With regard to the tensile test, the transverse rupture of tensile specimens generally occurs in the base metal. Only austenitic steels present a rupture close to the fusion line but at a breaking load very close to that of the base material. For materials with structural hardening, the rupture occurs in the molten zone. The tensile tests in the longitudinal direction are not carried out because of the difficulty in taking a test piece due to the narrowness of the molten zone.
Figure 2.37. CO2 laser beam weld of 12 mm thick non-alloyed steel (Institut de Soudure document)
Bend tests lead to good results. It should however be noted that in welds carried out on alloyed steels, the hardness difference observed in the weld area causes a deformation during the transverse bending test on either side of the molten zone. Longitudinal bend testing is thus more useful since it forces all the zones to deform in the same manner. For the impact test, a crack deviation and the absence of rupture is often observed in the test sample. This then raises the problem of the test’s validity. Palliative solutions have been developed to try to evaluate the strength of these welds. Currently there is no
76
Metallurgy and Mechanics of Welding
universal agreement, and further work is necessary to find a new test that is easy to carry out, inexpensive and gives valid results. The hardness test, which shows the various joint structures, are characterized by a lower value in the molten zone than in the heat affected zones (HAZ). This can be explained by a different cooling rate and the loss of quenching elements from the molten zone, such as manganese in steels. In arc welding processes, the hardness test is often associated with cold cracking and the threshold criterion of maximum hardness of 350 Vickers. For the laser and EB processes, this threshold is exceeded in the majority of cases. However, as the welding is performed in the absence of hydrogen since it is in a vacuum or under gas protection, the risk of cold cracking is almost zero, except for highly alloyed tempered steels or those with high levels of carbon. Fatigue resistance,is in general satisfactory, due to the presence of compressive stresses on the bead surfaces. 2.6. The quality of the assemblies The quality of a weld is measured with respect to its conformity to specifications imposed on the final assembly. It can be a question of its mechanical performance, water/air-tightness, or resistance to corrosion. Quality is tested overall using tests on the complete assembly or on the test specimens produced under the same operating conditions, and/or by observing this assembly in a very precise way, using both nondestructive and destructive tests. In the following section, we will present a non-exhaustive list of the possible defects in HEDB welds, the control methods most commonly used and the principal standards in operation. 2.6.1. Weld defects Standard NF EN 26520 is a “classification of the defects in the fusion welds of metals with explanatory comments” and makes it possible to enumerate and classify the defects according to their geometry, their position in the weld and their origin. HEDB processes, due to their particular features, give rise to the appearance of special defects. Cracks Hot cracks are most frequently encountered because of high solidification speeds and, in most cases, the absence of filler wire addition. They are emerging or
High Density Energy Beam Welding Processes
77
non-emerging and small in size. They are called hot cracks when they appear at the end of solidification on a molten pool. There are interdendritic or intergranular cracks, related to segregation phenomenon. The pulsed YAG laser beam welding process has a tendency to produce such defects in austenitic stainless steels, aluminum alloys and some nickel base alloys. The cracks are known as cold cracks when they appear towards the end of cooling, at around 150°C or less. These cracks are found in the molten zone or the heat affected zone. They are related to martensitic quench hardening, hydrogen embrittlement and internal stresses. Non-alloyed or low alloyed steels are sensitive to cold cracking according to their percentage of carbon and alloying elements. Various formulae have been proposed to define a weldability limit for these steels. Such formulae, established for conventional welding processes, only account for the composition of steels in terms of carbon equivalence but disregard the cooling speed. These formulae are not applicable in the case of HEDB processes because of its high cooling speed, and also the fact that they do not introduce hydrogen and that shrinkage stresses are limited. These cracks, encountered less frequently than hot cracks, are quite small. Cavities These are voluminal defects. They include shrinkage due to the shrinking of metal during solidification and often appear halfway down in the middle of the molten zone or in the craters at the weld end. Crater shrinkages are often accompanied by microscopic hot cracks. They are often observed in a widening of the molten zone or bulge related to poorly focused laser or electron beam. They are more often found in very thick components and when high levels of impurities, sulfur and phosphorus, are found in the alloy. They are aligned with the axis of the molten zone. Cavities also include the pores formed by gas trapped during solidification. They appear in the form of isolated pores or distributed along the weld zone. They are frequent in partial penetration welds. They occur more frequently when welding thick components and in cases of poor cleaning (aluminum alloys, titanium alloy). In laser and EB weld beads, their size can vary from a few tenths of a millimeter to a maximum of two millimeters, a result of the molten zone’s narrowness. They are located mostly half way down or at the weld root. Lack of fusion or penetration The lack of fusion is a lack of connection between the base metal and the weld zone. It is a flat defect. It can be related to a discrepancy between the beam and the weld seam. In the case of a heterogenous assembly, it is due to a significant
78
Metallurgy and Mechanics of Welding
difference in conductibility between materials. It is not easily detectable by non-destructive tests. Lack of penetration is a lack of fusion between the edges to be welded. It is located at the weld root. It is often caused by insufficient beam power or a degradation in beam focus. Shape defects We can distinguish the following defects: – undercuts: in the case of arc welding processes, these are due to a very localized lack of metal. They form an acute line on the surface at the front or on the reverse sides at the weld zone and base metal limits. In HEDB processes, undercuts are often due to a hollowing out of the weld bead on both sides of the molten zone. They are produced by an excessive power density or excessive welding speed. They are often encountered during the welding of titanium alloys; – insufficient thickness: this is caused by a collapse of the molten metal in the weld zone. There can be various causes: - a lack of material due to an excessive gap between the parts to be welded, - when welding very thick parts in flat position (the limits are: 20 mm for EB welding, 15 mm for laser beam welding), - an excessive power density; – misalignments: these are due to a shift in position between the two parts to be welded. This shift can lead to lack of weld root fusion. Projections (splatters) Metal splatter during welding can be adherent or not. It can be caused by excessive power density, the presence of organic materials on the surface of the part or in the seam, or an inadequate gas protection. The welding of nitrided or carbonitrided steels can cause these projections. 2.6.2. Weld inspection methods For HEDB welds, non-destructive tests make the detection of small defects possible. The welding speed requires the use of fast and inexpensive control test procedures. Controls can be carried out off-line (visual, radiography, ultrasound, magnetoscopy, Foucault current, etc.) or on-line (plasma analysis, infrared thermography, visually using a camera, etc.). In mass production, off-line control cannot be applied to all components, so on-line testing is preferred. Very often, an
High Density Energy Beam Welding Processes
79
on-line control is accompanied by sampling. In this case, a destructive test will be applied to a selection of parts. Destructive tests (clamped side stamping tests, metallography, etc.) are long and expensive. However, they make it possible to detect certain welding defects (cracks, lack of penetration or bond) and do not prejudge the total quality of the assembly. 2.6.3. Standardization and qualification of the welding operating mode EB welding has been the object of thorough standardization. Laser beam welding, a more recent process, is still in the process of standardization. The main welding standards are common today with ranges of different thicknesses for the two processes. The principal welding standards in force are as follows: – EN ISO 13.919-1: Welding – Joints welded by laser beam and electron beam – Guide to the quality levels of defects – Part 1: Steel; – EN ISO 13.919-2: Welding – Joints welded by laser beam and electron beam – Guide to the quality levels of defects – Part 2: Aluminum alloys; – EN ISO 15.609-3: Description of welding procedures by electron beam; – EN ISO 15.609-4: Description of welding procedures by laser beam; – EN ISO 15.614-11: Welding procedure test for electron beam and laser beam. 2.7. Economic aspects The main obstacle to the large scale development of HEDB processes is the operational and capital cost of this equipment. The investor must be certain of the technical advantage of the process but more especially its economic benefit. It is difficult to speak about costs for rapidly evolving processes. We will limit ourselves to touching on laser components and their operational and capital costs in order to give the reader the principal elements of any calculation [SAY 99]. 2.7.1. Cost of an electron beam machine The cost of a machine will vary according to the following factors: – technology selected: vacuum or non-vacuum, – electron acceleration voltage, – gun power,
80
Metallurgy and Mechanics of Welding
– enclosure volume, – displacement systems of the parts and the gun. It is difficult in these circumstances to estimate a price. To give some idea however, a machine equipped with a 30 kW gun and with a 1 m3 enclosure pumped in secondary vacuum will cost about €600,000. With regard to operating costs, the consumable costs are primarily electricity, cathodes and filaments whose lifespans vary according to use but can reach several dozen hours. The principal operating costs lie in maintaining the cleanliness of the enclosure and the gun, which has a very significant impact on the equipment productivity (a clean enclosure leads to reduced pumping times) and on the weld quality (a clean gun cuts the risk of beam interruption owing to lack of insulation). 2.7.2. Cost of a laser beam machine The hourly use rate of a laser system is mainly made up of paying off the capital cost, consumables, and the expenses of maintenance and labor. The most significant part of the total hourly rate is paying off the capital investment. Depreciation Companies tend to envisage increasingly shorter depreciation periods (less than 3 years). In the overall investment costs, it is necessary to take account of the laser source, the robot, the peripheral systems, the tools, the installation and integration expenses of the system. Consumables These depend on the laser system chosen. The CO2 laser system The “lasing” gas: consumption depends on the source type and the laser power. For lasers with fast axial flow, the gas outputs are low, about 30 l/hr for helium. Laser sources known as SLAB offer the lowest gas consumption. Shielding gas: the gas flow rates are about 15 to 30 l/min. The most expensive gas is helium; it is also the most frequently used because of its high ionization potential. Electricity: CO2 lasers have an electrical efficiency output of about 5 to 10%. The cost depends on the power used. It is important to take into account the consumption of the complete installation, cooler included.
High Density Energy Beam Welding Processes
81
Maintenance: this is estimated to be 5% of the annual capital investment. Optics: the cost of optics can increase significantly if the optical path is badly designed. It depends on the number of mirrors in the optical path, the type of mirrors and the protective systems used in the focusing head. It also depends on the procedure (clean parts, presence of oxides or oil) and on the operating environment. YAG laser system Lamps: the cost depends on the number of lamps employed and their lifespan. Lamps in continuous YAG lasers have an average lifespan of 1,000 hrs. The lifespan of the lamps depends on their use and can reach 2,000 hrs. For a pulsed YAG laser, the lifespan is given as a number of pulses. This can reach several million pulses. Shielding gas: argon is more easily usable than in the case of the CO2 laser. The gas flow rates are comparable. Electricity: a YAG lamp pumped laser has a lower electrical output efficiency than a CO2 laser, about 1 to 3%. A YAG laser diode-pumped laser offers a much better output of about 10%. Electricity consumption depends of course on the power of the laser. Fiber-optics: these should not deteriorate in normal use. It is however necessary to envisage their eventual replacement or repair. Focusing optics: these are very seldom replaced because of their glass protection. They are less expensive than lenses made of zinc selenium or mirrors. Protective glass: it is necessary to envisage the regular replacement of protective glass, at a frequency which will depend on the application. Currently the choice of a laser system is made at four levels: 1) choice of pulsed or continuous mode: this choice is determined by the type of application (material to be welded, thickness, distortion, etc) and by the production speed required; 2) choice of the laser type (YAG or CO2): flexibility (fiber or mirrors), thickness to be welded (powers available), materials (wavelength); 3) YAG laser pumped by lamps or pumped by diode: this issue is often raised because of the recent development of diode-pumped YAG lasers. The advantage of this laser is uncertainly its high quality beam. It is however necessary to make the comparison between the operating costs of both systems. A diode-pumped YAG
82
Metallurgy and Mechanics of Welding
laser does not require a change of lamps and its electrical output efficiency is higher. However, the high cost of laser diodes makes its capital cost much higher than that of a conventional YAG laser, which considerably increases its utilization cost. A reduction in the cost of laser diodes is expected, and this should reverse the trend; 4) choices of the mechanized system: the choice of a polyarticulated robot or a Cartesian robot will depend on the application and the choice of the laser type (YAG or CO2). It should be noted that the capital cost of a Cartesian robot is definitely higher than that of a polyarticulated robot. 2.8. Safety [HEE 00] The use of lasers in industry is recent and the technology is evolving quickly, which explains the regulatory weaknesses both in Europe and in France. The principal reference text is standard NF EN 60.825-1 “Safety of laser equipment – Part 1: Equipment classification, requirements and user guide”. Other specific standards cover particular questions such as: standard NF EN 12.626 December 1997 “Safety of machines. Laser machines. Safety regulations” and standards NF EN 207 “Laser safety glasses” and NF EN 208 “Safety glasses for laser adjustment”, December 1998. The principal risks when using a laser are to the eye. They derive from the physical characteristics of the laser. Certain radiations, according to their wavelengths, are transmitted to the retina and are focused by the crystalline lens. The power density received can be 5.106 times higher on the retina than on the cornea. The retina is particularly vulnerable to radiation from the visible or nearinfrared spectrum (0.4 to 1.4 Pm). If the density of energy received by the retina is excessive, it can cause an irreversible lesion. Standard NF EN 60.825 classes various lasers according to their risk. For EB welding machines, apart from the risks related to the presence of high voltages, which is controlled via the safety measures taken by the manufacturer, the principal risk is that of the production of x-rays, as previously mentioned. There again, the precautions taken by the manufacturer should be sufficient and are the subject of special attention at the time of delivery of the machine. It is thus incumbent on the user not to modify the equipment, particularly the enclosure without checking that the biological shields are properly in place.
High Density Energy Beam Welding Processes
83
2.9. Examples of industrial applications 2.9.1. Electron beam welding The industrial applications of EB welding are now well-known and encompass all the industrial sectors, from the automotive (transmission components) and aeronautical (manufacture of jet engines) to the manufacture of diverse parts or sensors (Figures 2.38-2.40).
Figure 2.38. Copper electrical connection (Techméta document)
Figure 2.39. Stainless steel turbine
84
Metallurgy and Mechanics of Welding
2.9.2. Laser beam welding We can list, in the following table, some well-known industrial applications. Application
Type of laser
Materials
Thickness
Automotive
CO2
Non-alloyed steels coated or not
0.7 to 2 mm
Bodyshells
Automotive
Continuous YAG
Coated non-alloyed steels
1.2 mm
Gear box pinions
Automotive
CO2
Non-alloyed steels
2 to 5 mm
Tubular radiators
Equipment
Pulsed YAG
Non-alloyed steels
1 mm
Pipings
Aeronautic
CO2
Titanium alloy
1 mm
Stiffeners
Aeronautic
Continuous YAG or CO2
Aluminum alloy
1 to 4 mm
Plate heat exchanger
Food
CO2
Stainless steels
1 to 2 mm
Casing closures
Electronics
Pulsed YAG
Aluminum, titanium, nickel alloys
1 mm
Oil filters
Automotive
Continuous YAG
Aluminum alloy
1 mm
Cardiac pacemaker
Medicine
Pulsed YAG
Titanium alloys
0.5 mm
Pipes
Iron and steel industry
CO2
Non-alloyed or slightly alloyed
5 to 16 mm
Power-assisted steering
Automotive
Continuous YAG
Non-alloyed steels
2 mm
Airbag initiators
Automotive
Pulsed YAG, continuous YAG or CO2
Aluminum alloy, stainless steels
0.5 mm
Welding of blanks
Industry
2.10. Development prospects The two processes are often presented in opposition. This does not appear realistic, each process having specific advantages which will make it better adapted to a particular industrial application.
High Density Energy Beam Welding Processes
85
Figure 2.40. Superconducting niobium cavity (Techméta document)
Figure 2.41. Automobile blank welding in aluminum alloy, 1.25 mm thick, power used 7.5 kW, welding speed 18 m.min-1 (igm Steigerwald Strahltechnik document)
Electron beam welding reached its zenith in the 1970s. The application fields were the nuclear, aeronautical and automotive industries. Its principal handicap is the vacuum enclosure. However, a renewed interest is currently noted with the development of new non-vacuum welding machines dedicated to automotive applications (see Figure 2.41). It should however be noted that, for several years, the appearance of sufficiently powerful laser sources has led, for certain applications, to the replacement of EB welding by laser welding because of an increased productivity related to the absence of pumping. The main instigator of developments in laser welding processes has been the automotive industry. After the welding of mechanical components (gear box pinions), the welding of thin sheet was developed. Steelmakers started by
86
Metallurgy and Mechanics of Welding
offering tailored welded blanks and today manufacturers invest in the spot welding of bodyshells on a continuous production line. Electron beam welding machines are no longer the focus of significant developments, whereas laser systems are evolving rapidly. Laser CO2 sources are more compact, and the beams are of higher quality. A significant effort is being made to reduce consumables. The most significant developments relate to YAG laser sources and diode lasers. The power of continuous Nd-YAG laser sources with cylindrical rods is technically limited to 5 kW, to obtain a beam quality compatible with transport by fiber-optics. The advent of laser diode pumped systems makes it possible to increase the power with equivalent beam quality. The ongoing developments in continuous YAG disk lasers will bring further improvements in beam quality and thus an increase in the power of these sources. Lasers using laser diodes also offer great promise, because of their high output and their low wavelength. Their use in welding is related to the improvement in the beam focus. Amidst development projects, peripheral systems are not to be ignored. These relate to joint monitoring systems and on-line test systems. To improve the productivity of the laser welding process, efforts to combine a laser beam with an electric arc are underway. This new welding process is called hybrid laser welding. The advantages of this process are numerous: – increase in acceptable gap between parts, – increase in welding speeds at equivalent laser power, – improvement of the laser/material interaction (aluminum alloys), – improvement of the metallurgy of welding by a reduction in the solidification speed, cooling rate and by the filler wire addition (reduction in the sensitivity to hot cracking). This process is promising. It should extend the range of laser applications. 2.11. Bibliography [BAR 98] BAROUILLET C., CHEHAÏBOU A., “Soudage par faisceau laser CO2 d’un acier inoxydable martensitique à durcissement direct – Influence de l’azote comme gaz de protection”, 6th CISFFEL, vol. 1, 1998.
High Density Energy Beam Welding Processes
87
[BOI 98] BOILLOT J.P., “La vision laser à haute vitesse, un atout indispensable pour…”, 6th CISFFEL, vol. 1, 1998. [CHE 93] CHEHAÏBOU A., GOUSSAIN J.-C., BAROUILLET C., “Etude de la sensibilité à la fissuration à chaud des aciers inoxydables austénitiques soudé par faisceau laser”, 5th CISFFEL, vol. 1, 1993. [CHE 98] CHEHAÏBOU A., GOUSSAIN J.-C., KNISPEL D., “Soudage par faisceau laser CO2 de différentes nuances d’alliages d’aluminum”, 6th CISFFEL, vol. 1, 1998. [COL 97] COLLECTIF, Etude du soudage par faisceau laser des aciers de mécanicien dans le cas d’un emboîtement – Investigation pour cerner la limite des nuances soudables, Rapport Institut de soudure no. 31729 (study financed by Cetim), November 1997. [DEL 56] DELONG W., OSTROM G., SZUMACHOWSXI E., “Measurement and calculation of ferrite in stainless steel weld metal”, Welding Journal, vol. 35, no. 11, 1956. [FRI 98] FRITZ D., LAZARENKO O.K., IRIÉ H., ABE N., OHMINE M., “Forty years of electron beam welding and material processing”, 6th CISFFEL, vol. 1, 1998 [HAV 96] HAVRILLA D., Laser welding design and process fundamentals and troubleshooting guideline, Document Rofin Sinar, May 1990, revised 19 April 1996. [HEE 00] HEE G., MEREAU P., DORNIER G., Les lasers, Document INRS ED 5009, 2000. [HER 86] HERZIGER G., “The influence of laser-induced plasma on laser materials processing”, in David Belforte and Morris Levitt (eds.), The Industrial Laser Handbook, Penwell, 1986. [MAI 84] MAILLET H., Le Laser – Principes et Techniques d’Application, Lavoisier, 1984. [MUR 94] MURRY G., “Soudage et soudabilité métallurgique des métaux”, Techniques de l’ingénieur, M 715, 1994. [POW 00] POWERS D., SCHUBERT G., “Electron beam welding: the useful tool for the automotive industry”, Welding Journal, p. 35-38, February 2000. [ROE 86] ROESSLER D.M., “An introduction to the laser processing of materials”, in David Belforte and Morris Levitt (eds.), The Industrial Laser Handbook, Penwell, 1986. [RYK 74] RYKALINE N. N., Les sources d’énergie utilisées en soudage, Assemblée annuelle de l’Institut international de la soudure, Doc. IIS/IIW-465-74, Budapest, 1974. [SAY 99] SAYEGH G., “Eléments à considérer dans l’évaluation économique d’un investissement laser”, LaserAP3, Sarlat, 1999. [SCH 49] SCHAEFFLER A.L., “Constitution diagram for stainless steel weld metal”, Metal Progress, vol. 56, no. 11, p. 680, 1949. [SUU 79] SUUTALA N., KUJANPAA V., TALAKO T., MOISO T., “Correlation between solidification cracking and microstructure in austenitic-ferritic stainless steel welds”, Welding Research Int., vol. 2, p. 55, 1979.
This page intentionally left blank
Chapter 3
Thermal, Metallurgical and Mechanical Phenomena in the Heat Affected Zone
As a general rule, welding operations modify the metallurgical structures and the local properties of the assembled parts deeply. In certain extreme cases, they can be at the origin of defects such as cracks, porosities or local embrittlement. Consequently, it is important to thoroughly understand the influence of various factors such as the thermal welding cycles and the chemical composition of the parts to be assembled. In this chapter, we will successively examine: – particular thermal phenomena associated with the operations of welding; – the microstructural modifications and principal metallurgical consequences associated with these thermal phenomena; – the modifications of the mechanical properties in the zone adjacent to the molten metal, i.e. in the heat affected zone (HAZ). 3.1. Thermal aspects related to welding In spite of their great diversity, the welding processes have localized heat concentration as a common characteristic.
Chapter written by Dominique KAPLAN and Guy MURRY.
90
Metallurgy and Mechanics of Welding
A welding operation can thus be described as a short passage of a small amount of matter at a very high temperature followed by a cooling, primarily by conduction in the adjacent parts: cooler adjacent metal, clamping tools, electrodes (in the case of spot welding). The thermal cycle at any point close to the welded zone thus represents the heat dissipation associated with the welding, and thus depends on variables related to the process (quantity of effective heat applied), on the material (thermal conductivity) and the configuration of the assembly. This localized heating can be carried out without displacement of the heat source (in the case of resistance or aluminothermic welding) or by displacement of the source relative to the part (in general arc and laser welding). In the second case, if a constant rate of travel is considered, the thermal characteristics of a quasi-stationary mode, where the temperature redistribution around the source adopts a stable form in relation to time, can be determined. A resolution of the simplified heat equation was proposed by Rosenthal [ROS 46] as early as 1935, followed up by Rykaline [RYK 61], Clyde and Adams [CLY 58]. The principal points are the following: if one imagines a specific heat source q moving at a constant speed along an axis x, the differential heat equation is written, in a series of coordinates (x,y,z) (see Figure 3.1):
§ w ²T w ²T w ²T · ¸¸ © wx ² wy ² wz ² ¹
D ¨¨
wT wt
[3.1]
with: – T : temperature; – t: time; –D: thermal diffusivity (m2 s-1) of material = O/pC, with: - O: thermal conductibility (J m-1°K-1s-1), - UC: voluminal calorific capacity (J m-3°K-1). A system of mobile coordinates can be defined related to the source by posing: [ = x - vt. In stationary mode (
wT = 0), the preceding equation then becomes: wt
Thermal, Metallurgical and Mechanical Phenomena
§ w ²T w ²T w ²T · ¸¸ © w[ ² wy ² wz ² ¹
D ¨¨
§ wT v¨¨ © w[
· ¸¸ ¹
91
[3.2]
Figure 3.1. Definition of the system of co-ordinates where a heat source moves at a constant speed v
Figure 3.2. Diagrammatic flow of heat in the case of welding “thick” (a) or “thin” products (b)
Equation [3.2] can be solved by considering two distinct situations (see Figure 3.2). In the case of welding “thick”1 products, the dissipation of heat occurs primarily radially compared to the source. At any point, the change in temperature according to time and the distance is expressed: r²
T
q v 4Dt T0 e 2SOt
1 The notions of thin or thick products will be quantified more precisely later.
[3.3]
92
Metallurgy and Mechanics of Welding
with: – r: outdistance point considered compared to the source of heat (r =
([ ² y ² z ² );
– q: calorific contribution (J); – v: rate of travel of source (m/s). The q/v term indicates linear energy or the quantity of heat introduced per unit of length of the welded joint; – T 0: initial temperature. In the case of welding thin products, the heat dissipation is negligible in depth. The isotherms are thus perpendicular to the surface of the parts. A simplified solution of equation [3.2] is written:
T
T0
q v d (4SOUCt ) 1 2
e
r² 4Dt
[3.4]
where d indicates the thickness of the welded parts. Portevin and Séférian [POR 34] put forward a pictorial image, a thermal solid, to represent welding temperatures in spatial terms, expressed in equations such as [3.3] or [3.4]. Figure 3.3 presents the example of such a diagrammatic representation, axis Ox indicating the welding direction (x indicating distance as well as time), axis Oy the distance to the axis of the welded joint, and the axis Oz the temperature. With a given distance from the axis (y1 fixed), the thermal cycle T (t) is described by the intersection of the thermal solid with the plane parallel to (xOz) in y1. In the same way, at a given temperature T 1, the form of the isotherm is described by the intersection of the thermal solid with a plane parallel to (xOy) in T 1. It is precisely by using this last representation that the differences in temperature distribution during welding of thin or thick products can be appreciated (see Figure 3.4). It will thus be observed that the network of isotherms is much denser upstream of the passage of the heat source, which translates to the fact that the rise in temperature (heating phase) is faster than the descent (cooling phase).
Thermal, Metallurgical and Mechanical Phenomena
93
Cross-section of isotherms at different distances y
Figure 3.3. 3D representation of welding temperature distribution in the case of a mobile source; from [EAS 83]
Because of the finite speed of heat propagation, all the fibers parallel with the welding axis do not simultaneously reach their maximum temperature. The plot of points corresponding to this maximum is the curve (m). Compared to the direction of displacement of the source of heat, all the points upstream of this curve are in the heating phase, and behind, in the cooling phase. The cooling and heating rates are correspondingly greater as the linear energy (q/v) is weaker or the products are thicker and the conductibility greater. In the case of welding of thin products, the temperature distribution is more spread out in the longitudinal and transverse direction than in the case of thick materials. The difference derives from the possibility, in this last case, of heat dissipation throughout its depth. Compared to materials with lower conductibility (e.g. austenitic stainless steel, O # 0.02 Wmm-1°C-1), the welding of material such as aluminum (O # 0.23 Wmm-1°C-1) leads to a widened isothermic distribution, albeit less extended in the longitudinal direction of the source displacement.
94
Metallurgy and Mechanics of Welding
Figure 3.4. Example of temperature distribution during the welding of (a) thin or (b) thick sheet steel assembled under identical conditions; from [EAS 85]
At this stage, we must keep in mind that the analytical calculations presented rest on many assumptions (specific heat source, thermal properties independent of temperature, ignoring latent heat due to phase transformations and heat losses by convection or radiation, etc.). Although new digital methods (see for example [GRO 94, KOV 86, WEI 95, ZAC 93]) allow for a more complete consideration of parameters, experience shows that this simplified approach makes it possible to solve the great majority of problems with satisfactory precision.
Figure 3.5. Diagrammatic representation of the thermal cycle in HAZ. Definition of the parameters T M,
700 800 , 't 500 't 300
Thermal, Metallurgical and Mechanical Phenomena
95
We will now reconsider the thermal cycleT (t) applicable at any point of the HAZ. Whatever the type of welding process (fixed source or mobile), it typically comprises (see Figure 3.5): – a very fast heating phase, of which the mean velocity is typically from some 102°C/s (arc welding), rising to 104°C/s for the HDE processes such as laser welding [DEV 89]; – a passage at a maximum temperature TM. In general, the duration at this temperature is very short, and is all the more reduced the higher TM is; – a more or less fast cooling phase. To simplify matters, we generally characterize the intensity of this cooling by time passing between two given temperatures: 800
- either between 800 and 500°C, the cooling parameter is then 't 500 , 700
- or between 700 and 300°C ( 't 300 ). The relationship between this parameter and the previous one generally lies between 2 and 4. The choice of these two criteria was guided in particular by the fact that the majority of metallurgical transformations occur in these two temperature ranges in the case of carbon-manganese steels. Experience actually shows that the final metallurgical structure at any point of the HAZ depends almost entirely on the maximum temperature T M reached at this 800
point, and on the cooling parameter as defined by 't 500 . Certain thermal aspects concerning these two parameters will now be more fully developed. 3.1.1. Maximum temperature attained in the HAZ It was seen that expressions like [3.3] and [3.4] described the temperature change according to time in the respective cases of welding thick or thin products. The maximum temperature is reached at a time tM such that:
wwșt
tM
= 0.
Moreover, in order to avoid the singularity (T M o f ) when (rĺ0), the limiting condition is imposed: T M = Tf, melting point, when r = R, radius of the molten metal deposit.
96
Metallurgy and Mechanics of Welding
We are then led to the following expressions: – maximum temperature attained in the case of thick sheet welding (twodimensional flow of heat in a section perpendicular to the welding direction):
1 T M T 0
SeUC ( r 2 R ²) 2q v
1 T f T 0
[3.5]
– maximum temperature attained in the case of thin sheet welding (unidimensional flow of heat in a section perpendicular to the welding direction):
1 T M T 0
2Se UCdr 1 q v T f T 0
[3.6]
Figure 3.6. Evolution of peak temperature according to the distance to the fusion line. Comparison of the analytically calculated temperatures and those recorded in experiments (submerged arc welding); from [DEV 87]
Thermal, Metallurgical and Mechanical Phenomena
97
Thus, the maximum temperature in the HAZ varies in approximately inverse proportion to the distance r to the fusion line (i.e. in thin materials) or to its square (i.e. thick materials). In the case of plates, the maximum temperature reached does not depend on the product thickness. In spite of their simplicity, these expressions generally give a good account of the maximum temperature evolution in the HAZ, as Figure 3.6 testifies. This presents a comparison of experimental data recorded by thermocouples of thermal cycles in the HAZ, with the results of an analytical calculation (welding of thick products in the case presented here). 3.1.2. Cooling parameter in the HAZ With the maximum temperature, the cooling speed, quantified by the parameter 't , is the most significant determining factor for the metallurgical structure of 800 500
the HAZ. Expressions [3.3] and [3.4] make it possible to calculate: – the cooling parameter associated with thin sheet welding: 800 (q / vd )² ª 't 500 = «
º 1 1 » 4SOUC ¬ (500 T 0 )² (800 T 0 )² ¼
[3.7]
(temperatures expressed in °C); – the cooling parameter associated with thick sheet welding: 800 q/v ª = 't 500 «
º 1 1 » . 2SO ¬ (500 T 0 ) (800 T 0 ) ¼
[3.8]
Readings of thermal cycles taken for welded joints [DEF 75, MUR 67] show that the cooling parameter varies very little within the same welded joint. In this way, it can be said that the various zones of a welded deposit can be characterized by a 800
700
single cooling parameter value 't 500 (or 't 300 ). The continuing evolution of the microstructure thus depends only on that of the maximum temperature reached locally, all the points undergoing a practically identical cooling rate. It now remains to link the cooling parameter to the welding conditions in a more precise way: if welded joints are produced, starting from products of various thicknesses while varying the linear energy of welding, the variation of the cooling parameter associated with these conditions is presented in Figure 3.7.
98
Metallurgy and Mechanics of Welding
Figure 3.7. Influence of the thickness and linear welding energy on the cooling parameters
Beyond a certain thickness, the cooling parameter does not vary. This critical thickness, called the thickness limit, is correspondingly higher the greater the welding energy is. From the point of view of welding, a product will thus be regarded as “thick” for a given energy of welding, if its thickness is higher than the thickness limit. In reality, this concept of thickness limit represents the modification of the nature of heat dissipation in the welded joint: below the limit, the flow of heat is twodimensional, with normal isotherms compared to the plane of the product. Beyond this, the flow is three-dimensional and the isotherms take on a cylindrical form. There exists a zone of transition between these two modes, where the isothermal form is affected by radiation to the lower part of the component. In practice, it is important to define the welding linear energy (term q/v in the preceding expressions) encountered in this phenomenon. This is the product: – of linear electrical energy Ee, defined from the welding parameters: for example, in arc welding, carried out with a voltage U and current intensity I, the UI , E being frequently expressed in kJ/cm; expression can be written: Ee v – of a thermal efficiency coefficient KP, intrinsic to the welding process used, which characterizes the relationship between the energy actually transferred to the part and electrical energy. Table 3.1 indicates generally accepted values.
Thermal, Metallurgical and Mechanical Phenomena Welding process
Thermal efficiency Șp
Submerged arc welding
0.9 to 1
Welding with coated electrode
0.7 to 0.85
MIG welding
0.7 to 0.85
TIG welding
0.2 to 0.8
Electron beam welding
0.8 to 0.95
Laser
0.4 to 0.7
99
Table 3.1. Thermal efficiency coefficient of various welding processes; from [CHR 65, CON 87, DEV 85, GRO 94, ION 97, NIL 75]
It will be noted that TIG welding’s efficiency is generally low and varies with many factors: intensity, DC or AC, shielding gas, etc. In the same way, the efficiency of laser welding is very variable according to the reflectivity of the part: low for copper or polished aluminum parts, the efficiency (and thus the beam penetration) can be increased by depositing a fine layer of graphite or zinc phosphate. The linear welding energy is also the product of a coefficient KG related to the geometry of the deposit and assembly. By definition, a flat deposit (heat diffusion at an angle of 180°) will be expressed as: KG = 1. A T-shaped assembly (diffusion of heat at 270°) will be characterized by the coefficient 180 2 KG = . This approach can be generalized for more complex examples 270 3 (preparation of X-shaped, V-shaped chamfers, etc.). The effective linear welding energy is then written: E = ȘP u ȘG
UI . v
This value, as well as the thickness of the welded products, makes it possible to define the thermal welding mode: in a remarkable study [BER 72] based on a theoretical and experimental approach, G. Bernard could specify the field of thick and thin products with respect to welding heat dissipation.
100
Metallurgy and Mechanics of Welding
Figure 3.8. Graph determining the cooling parameter
800 't 500
according to the welding conditions; from [ATS 80]
Thermal, Metallurgical and Mechanical Phenomena
101
In the absence of pre-heating (T 0 = 20°C), a part will be regarded as thick based 800
on the criterion 't 500 if its thickness d (mm) is such that: d > 4.5
E 700
E being expressed in kJ/cm. In the case of the criterion 't 300 , this condition would be written: d > 6.35
E
From such criteria, it is then possible to calculate the 't parameter values according to expression [3.7] or [3.8]. To enable rapid estimations, IRSID [ATS 80] developed a forecast graph of the 800
value of 't 500 starting from the various parameters in the case of arc welding (see Figure 3.8). Thus, as an example, we can consider a TIG welded joint with an UI energy of 15 kJ/cm on a T-shaped assembly. Starting with electrical energy v (point A), corrections related to the geometry of the assembly (point B) and to the efficiency of the process lead to an effective energy E (point C) of 5 kJ/cm. Under these conditions, the welding of 8 mm thick materials will lead to a value of 800 of 4 seconds (D). 't 500 Another example (MIG welding at 20 kJ/cm) shows how it is possible to take account of the pre-heated temperature T0 (here 200°C) by a correction of the thickness and effective energy. As an indication, Table 3.2 gathers some typical values of cooling speeds observed for various welding processes, in the range of thicknesses used in these processes. Welding resistance
TIG,
process
(spot,
ERW,
roller…)
plasma
600°C), certain phenomena such as tempering, the spheroidizing of the cementite lamellae, the recrystallization in the case of welding of strain hardened products, ageing, etc., can possibly occur [GRA 95]. We also have a partial transformation zone (or intercritical zone), between A1 and A3 (§ 830°C for the composition considered). In this field ferrite coexists with a newly formed phase, austenite J, a solid insertion solution of cubic centered face structure. It is starting from this zone (T > A1) that the heat affected zone begins. From temperature A3 up to approximately 1,495°C, the transformation into austenite is total. The new structure thus replaces and erases any trace of the former ferritic structure. It is within this zone that an austenitic grain enlargement occurs: this is of a very small size at temperatures slightly higher than A3, and can reach a few hundred microns for the highest temperatures. In this case, the term employed is coarse grain zone (for example, when the austenitic grain size exceeds a few tens of microns) and in general it is this zone which is the most likely to cause certain metallurgical problems, as will be seen later. We have another zone partially in the liquid state, where a solid ferritic phase (G) and a liquid phase coexist. Very small in size (and thus difficult to observe micrographically), this zone constitutes the connection between the base metal and the molten metal. On the balance diagram, this corresponds to the temperature interval between the beginning and the end of fusion (solidus-liquidus interval). Certain phenomena (local decarburization by enrichment of the liquid in the solute, intergranular liquation by eutectic formation at low melting point in the case of impurities, etc. [GRA 95, HAL 84]) can intervene in this bond zone. Finally, the molten metal often has a composition different from that of the base metal, because of the volatilization of certain elements, reactions with the surrounding medium, or of enrichment by external elements (filler material). The first molten metal nuclei are solidified by epitaxy (crystallographic coherence) on the grains of the HAZ. At this stage, it is necessary to note the following points: – the transformations and temperature ranges evoked above correspond to a state of balance. In reality, the brevity of the thermal cycles means that phase
104
Metallurgy and Mechanics of Welding
transformations and structural homogenity intervene at temperatures sometimes considerably higher than these balanced temperatures; – the particular case considered here (alloy Fe-0.15% C) presents a situation where phase shifts occur during heating. In the case of other materials (for example: aluminum alloys, copper, ferritic stainless steels, etc.), the thermal welding cycle intervenes in a single-phase area. A grain enlargement will then be found throughout the cycle, without possibility of refinement by phase shift; – starting from expression [3.5] or [3.6] and the knowledge of the phase transformation temperatures, it is possible to predict the HAZ width in various conditions of welding. The calculations, confirmed by observations of welded joints, show that this can vary from a few hundreds of microns (for example: low power densities in laser welding [ION 97] and resistance welding [CHA 74]) to 15 mm in electroslag welding [DEB 82, HAR 80]. In addition to these microstructural modifications, welding operations have a marked influence on the precipitates possibly present in the base metal. Indeed, it is known that modern steels draw their mechanical properties (resistance, ductility, toughness) from an optimized combination of hardening, by the nature of the microstructure, the grain and precipitation refinement. This balance is significantly modified by the thermal welding cycles. Generally, the dissolution of various particles (carbides, nitrides, sulfides, oxides) can be quantified, starting from the variation of their solubility product with the temperature, described in this form (case of diluted solutions) [RIS 74]: MaNb aM + bN, a and b defining the stoichiometry of the initial compounds: log [%M] a [%N] b =
B 'Go =A– RT T
'G 0 indicates the free energy of the reaction, T the absolute temperature, R the constant of perfect gases (1,987 cal. K-1 mol-1). Table 3.3 and Figure 3.10 present the solubility product of some compounds, from which the temperature at which they are totally soluble can be calculated.
Thermal, Metallurgical and Mechanical Phenomena
Type of precipitate
A– B
NbN VN AlN TiN TiC NbC MnS Al2O3 SiO2 MnO Ti2O3
4.04 – 10230/T 3.02 – 7840/T 1.79 – 7184/T 4.35 – 14890/T 5.33 – 10475/T 2.26 – 6770/T 2.93 – 9020/T 20.43 – 125986/T 5.10 – 44801/T –5.71 – 24262/T 16.18 – 104180/T
105
T
Table 3.3. Expression of the solubility product of various compounds in austenite; concentrations in % by weight, T in °K
The higher the temperature reached locally in the HAZ, the greater the likelihood of precipitates decomposing. In decreasing order, the stability of these compounds is as follows: oxides, nitrides, sulfides, carbides. For common compositions of structural steels, decomposition of carbides in the HAZ will be observed around 1,100-1,150°C (VC, TiC) [HRI 95], nitrides around 1,150 to 1,300°C, sulfides being generally dissociated around 1,100 to 1,200°C. Taking into account their very strong stability, oxide inclusions resulting from the steel making in the liquid state (alumina, silicates, etc.) are not affected by the welding cycle. Being very few, and relatively large in size (for example: several tenths to a few microns), these oxides generally do not play a role at the time of the heating phase in the HAZ. It is not the same for nitrides or carbo-nitrides. Indeed, it is known that these numerous, fine and dispersed particles slow down the growth of austenitic grain since the joint displacement this achieves is accompanied by a local increase in enthalpy.
106
Metallurgy and Mechanics of Welding
Figure 3.10. Solubility products of various compounds in austenite
Maximum size of grains dmax , in the presence of a population of precipitates of size r and whose voluminal fraction is VF, can be expressed by the Zener relation 4r . [ZEN 48]: d max 3V f In general, an increased austenitic grain size in the HAZ leads thereafter to a coarser ferritic structure. To limit this phenomenon, it is possible to show that low additions of titanium (an element which forms, as was seen previously, very stable nitrides at high temperature) slow down the growth of the austenitic grain effectively (see Figure 3.11). It should however be stressed that this result is obtained only if these nitrides are relatively fine (a few tens of nanometers), i.e. primarily if they are formed after solidification during steelmaking and not in the form of coarser precipitates (micrometric particles, formed in the molten metal).
Thermal, Metallurgical and Mechanical Phenomena
107
Figure 3.11. Influence of maximum temperature on the austenitic grain size in HAZ of steels containing various types of precipitates; from [KAN 76]
3.2.2. Transformations in the HAZ during cooling In the case of structural steels, the microstructures observed in the HAZ of welded joints correspond to transformed products of austenite. It is in fact difficult to study these metallurgical transformations starting from traditional CCT diagrams (continuous cooling transformation). Indeed, these are generally established starting from austenitic treatments at a relatively low temperature (900-950°C) and for long durations, i.e. a situation exactly opposite to that encountered in the HAZ. In order to consider more representative conditions, the metallurgical phenomena starting from thermal heating and cooling cycles very close to those met in welding are studied. These tests are generally carried out on specific thermal simulators (Gleeble and Smitweld simulators, etc.). For a given material (see Figure 3.12) and austenitization conditions (temperature generally higher than 1,200°C, so as to simulate the HAZ with coarse grains), the transformations of the austenite according to the cooling speed using the CCT diagram in welding conditions or more simply of the evolution of hardening the final microstructure with temperature can be gathered.
108
Metallurgy and Mechanics of Welding
Figure 3.12. (a) Example of CCT diagram in welding conditions (T M = 1,300°C); (b) corresponding graph (hardness-criterion of cooling 't). Steel C = 0.18%, Mn = 1.4%, Si = 0.4%
According to the cooling speed, various types of microstructures are liable to be formed. For very high speeds (lower than the critical quenching rate VCM, which corresponds to a plateau on the hardness-criterion cooling graph or HV-ǻt), martensite appears. Having a tetragonal crystallographic structure, this supersaturated solid solution of carbon in iron is formed by a shearing mechanism without atomic diffusion. Identical in composition to that of the mother austenite, martensite has a hardness HVM which depends virtually only on the percentage of carbon in the steel alone, according to the expression: HVM=283+930(%C) [IRS 77]2. At intermediate speeds, bainitic structures appear. Formed starting from metastable austenite at temperatures too low for the carbon to be able to diffuse at the grain boundaries, the bainite is characterized by the very fast growth of ferrite needles by shearing and a precipitation of carbides. Without returning to the complex debate relating to the description of bainitic structures (see for example [BHA 97, HEH 72, HON 95, OHM 74]), we will simply recall that faster cooling 2 Other similar expressions have been proposed: HVM = 293+812(%C) (Satoh), 305+802(%C) (Duren) or HVM= 294+884[%C(1-0.3 (%C))²] (Yurioka), etc.
Thermal, Metallurgical and Mechanical Phenomena
109
speeds lead to the formation of the harder lower bainite structures (carbide precipitation in the shape of thin platelets within the ferrite laths), whereas slower speeds are associated with higher bainite formation (carbides rejected from the ferrite lath joints, sometimes in the form of quasi-continuous cementite lamellae [CON 92]). In this last case, the local carbon content can be such that the formation of compounds between the laths occurs where martensite and austenite coexist (M-A compounds), the latter being stabilized because the transformation temperature Ms is lowered below room temperature [AND 65]. Slower cooling speeds in welding correspond to the precipitation of proeutectoïd ferrite at the old austenitic grain boundaries and the evolution towards a ferritoperlitic structure. It is also in this range of cooling speeds that some compounds (vanadium and niobium nitrides or carbo-nitrides, etc.), dissolved at the time of the heating phase, can re-precipitate in a more or less complete form. Various more or less complex formulae have been proposed in order to describe the evolution of HVmax hardness in the large grained HAZ of C-Mn steels according to their composition and the speed of cooling. We can for example quote that of Yurioka [YUR 87], applicable to steels of less than 0.3%C, 5%Ni, 1%Cr without B 800
( 't 500 expressed in s, content in %): HVmax= 206 + 442 C + (402 CEI – 90 CEII + 80) arctan (x) + 99 CEII with: CEI = C
Mo Mn Cr Ni Cu Si 4 6 8 12 15 24
CEII = C
Mo Nb Mn Cr V Cu Ni Si 2.5 3 5 10 18 24
x=
CEIII = These expressions reveal the concept of carbon equivalent (CE, a function of the level of C, M, Mo, etc.), which will be subject of further discussion in connection with cold cracking. At this stage, it must be retained that it is a factor quantifying the
110
Metallurgy and Mechanics of Welding
capacity for hardening. At a given cooling speed, limiting hardness amounts to limiting the percentage of carbon equivalent. As has been previously stressed, the microstructure formed at any point of the HAZ depends on the temperature reached locally. Figure 3.13 illustrates, in the case of a 32C1 steel, the influence of the temperature on the transformation of austenite. 700 108 cycles.
Figure 6.27. Catalog extract and S-N design curve
The quality of the weld must conform to that required by the current welding regulations.
Fatigue Strength of Welded Joints
231
6.2.3. Verification methods In the case of constant amplitude loading, checking or dimensioning a fatigue welded structure amounts to checking the following expression: (for a given number of cycles , n) knowing that: 'V S ,k .J F d
'V R , k JM
°'V S ,k stress range applied to the structure (loadings), JF safety factor ® °¯'V R,k design stress range, JM safety factor or to check n d N with n the number of cycles applied and N the number of cycles to failure for stress 'Vs.
'V 'V
Figure 6.28. Checking welded structure under fatigue conditions in the case of constant amplitude loading
The general methodology of fatigue verification is described in Figure 6.29. Advantages and disadvantages
This method is relatively simple to use if the nominal stress is clearly defined and the type of assembly indexed in the catalog. On the other hand, in the general case (complex structure/loading), the nominal stress cannot always be defined in terms of the resistance of materials and the reference frame is unknown. Moreover, nominal stress does not take account of the assembly’s geometry. For example, it does not consider the presence of a welded fastener, or of that of the corresponding weld bead, and therefore of the stiffness imparted by them. This is why an S-N curve exists for each type of assembly and that, for the same assembly, there can be several curves, depending on the dimension of the assembly and the type of loading.
232
Metallurgy and Mechanics of Welding
Figure 6.29. Logigram of the general method
6.2.4. Geometric structural stress method 6.2.4.1. Principle of the method It thus seems sensible to use another stress definition that takes account of the geometric effects of the welded connection, which includes not only the total geometry of the assembly but also the shape of the weld bead, the profile of connection between this bead and the base sheet metal, and, possibly of very local notch effects (see Figure 6.30). Nevertheless, the definition of local stress is fraught with difficulty, both experimentally and in calculation; moreover, such a stress is random in value because of local geometric variations caused by welding operations. It is however obvious that the value of this local stress governs the fatigue life of the assembly to a certain extent. This stress particularly influences the duration of fatigue crack initiation. Consequently, an intermediate step consists of adopting as a dimensioning stress the geometric stress, VG, which depends only on the assembly’s geometry and loading. This method applies only for initiation at the weld toe, where the concept of geometric welding quality has some relevance.
Fatigue Strength of Welded Joints
233
The advantage of establishing S-N curves in geometric structural stress, as compared to existing curves which are established in nominal stress, is that we are then able to use only one S-N curve whatever the loading and whatever the geometry, for the same group of assemblies (for example fillet welds). Moreover, for real structures, where the nominal stress (distant stress) is often difficult to define, in particular because of the proximity of other connections, the geometric structural stress can be evaluated starting from finite element calculations on the whole of the structure and the assembly under consideration. Moreover, starting from these S-N curves, certain assembly configurations not currently in the codes can be dimensioned. Thereafter, the use of the geometric structural stress makes it possible for S-N curves to be determined according to the welding quality, and thereby account for the local geometry of the weld bead. However, there is not, at present, any general method to determine the geometric structural stress nor an associated S-N curve to cover every type assembly group for welded plates. On the other hand, such a method is clearly defined and used in the case of tubular assemblies in offshore oil rig construction, and in the case of assemblies of thin sheet steel in the automotive field [FAY 95].
Figure 6.30. Definition of local (VL ), geometric (VG) and nominal (Vn) stresses (example: assembly subjected to bending stress)
Figure 6.31. Stress gradient, extrapolation
234
Metallurgy and Mechanics of Welding
6.2.4.2. Definition of geometric stress In Eurocode 3, the geometric stress is defined as: “the maximum principal stress in the parent metal, at the weld toe, taking into account the effects of stress concentration, due to the overall geometry of a particular detail of construction, but excluding the effects of local stress concentration, due to the geometry of the welding and discontinuities in the bead and the adjacent parent metal”. Geometric structural stress is thus an aspect of design or dimensioning which takes account of the total geometry of the assemblies and the loadings; it thus does not have a physical meaning since it does not take account of the actual weld geometry of the bead. It is determined right from the weld toe, as representative of the stresses at the intersection (see Figure 6.31). It can be obtained numerically by using the finite element method. The advantage of the finite elements method lies in it allowing the definition, not only of the maximum stress value, but also the point of greatest loading (hot spot) as well as the the stress field configuration throughout the structure. Possible fields of application In the case of structural analyzes, where the nominal stress is easy to determine and where the object to be calculated exists in procedural catalogs, the traditional method (S-N curve in nominal stress) can be used. In the other cases, the geometric structural stress must be determined starting from a finite elements calculation, and this must be associated with S-N curves determined with the same definition of the geometric structural stress. Determination of structural geometric stress The finite elements method used must satisfy two criteria: – evaluate a stress field, in the vicinity of the weld toe, as near to reality as possible, – lead to a fast and inexpensive application. For this, the type of element selected must be as simple as possible. All the elements located along the intersecting line of a surface must have the same dimension, or at least be in the direction perpendicular to the intersection; it is thus possible to the results being undesirably affected by the mesh size. In addition, it is important that the points where the stresses are calculated (Gaussion points) are correctly placed, i.e. outside the zone which has a 3D behavior, and if possible directly associated with the weld toe.
Fatigue Strength of Welded Joints
235
6.2.4.3. Practical use of the method The method of geometric constraint applies to the points described hereafter. Definition of the S-N design curve in structural geometric stress The S-N design curve, in structural geometric stress, can be determined starting from tests carried out on assemblies for which the extent of calculated or measured stress is expressed in geometric stress and the number of cycles is that defined for this level of stress range according to the failure criterion [HUT 92]. Figure 6.32 presents the steps followed to determine the S-N curve, in structural geometric stress.
Figure 6.32. Procedure followed to determine the S-N curve in geometric stress
Figure 6.33. Procedure followed to determine the fatigue life of the assembly
236
Metallurgy and Mechanics of Welding
Figure 6.34. Procedure followed to deduce the new S-N curve of the subject considered
Calculation of the fatigue life of an assembly Knowing the S-N curve in geometric (structural) stress for the type of assembly to be checked, the geometric stress method makes it possible to determine the fatigue life of the assembly, N (see Figure 6.33). Determination of the S-N design curve in nominal stress, of a new construction detail In the absence of experimental results, the geometric (structural) stress method can be applied to the determination of the S-N design curve, in nominal stress, of a construction object close to a case of the standard catalog or of the regulations [HUT 92]. In this case, we initially proceed with numerical modeling, both of the assembly considered and that of the catalog, before deducing the new S-N curve of the subject under consideration (see Figure 6.34).
Fatigue Strength of Welded Joints
237
6.3. Bibliography [COL 82] COLLECTIF, La résistance à la fatigue des assemblages soudés à l’arc en acier de construction métallique, Collection ATS-OTUA, 1982. [COL 85] COLLECTIF, Guides pratiques sur les ouvrages en mer, Assemblages tubulaires soudés, Editions Technip, 1985. [CTI 00] CTICM, Recommandations pour la conception en fatigue des assemblages et des composants soudés, IIS – Document XIII – 1539-96, CTICM, 2000. [EUR 92] EUROCODE, Design of Steel Structures – Chapter 9: Fatigue EUROCODE 3 (1992). [FAY 95] FAYARD J.L., BIGNONNET A., DANG VAN K., “Fatigue design of welded thin sheet structures”, Fatigue Design 95, vol. II, September 1995. [GUR 79] GURNEY T.R., Fatigue of Welded Structures, Cambridge University Press, 1979. [HUT 92] HUTHER M., PARMENTIER G., HENRY J., Hot spot stress in cyclic fatigue for linear welded joints, IIS – Document XIII – 1466-92, 1992. [HUT 94] HUTHER I., PRIMOT L., LIEURADE H.P., JANOSCH J.J., COLCHEN D., DEBIEZ S., “Influence de la qualité de la soudure sur la résistance à la fatigue d’un acier HLE du type E460”, Tôle en acier HLE, choix et mise en volume, Publications CETIM, 1994. [HUT 99] HUTHER I., GORSKI S., LIEURADE H.P., LABORDE S., RECHO N., “Longitudinal nonloaded welded joints, geometric stress approach”, Welding in the World, vol. 43, no. 3, p. 20-26, 1999. [LIE 73] LIEURADE H.P., “La résistance à la fatigue des assemblages soudés”, Journées “Métallurgie du soudage” (Société Française Métallurgie), Marseille, 8-9 November 1973. [LIE 91] LIEURADE H.P., BIGNONNET A., “Les techniques d’amélioration de la tenue en fatigue des composants soudés”, Traitements de surface et composants mécaniques, Editions CETIM, p. 79-112, December 1991. [LIE 92] LIEURADE H.P., WYSEUR M., TOURRADE J.C., “Effet de traitements de parachèvement sur le comportement en traction ondulée ou en flexion ondulée d’assemblages bout à bout en acier E 490”, La fatigue des composants et des structures soudés, Publication CETIM, 1992. [LIE 97] LIEURADE H.P., “Rôle des contraintes résiduelles dans le comportement en fatigue des composants soudés”, Revue Française de Mécanique, no. 1997-3, p. 191-205, 1997. [LIE 00a] LIEURADE H.P., HUTHER I., “Introduction aux méthodes de dimensionnement à la fatigue des composants soudés”, Mécanique et Industrie, vol. 1, no. 5, p. 465-477, 2000. [LIE 00b] LIEURADE H.P., HUTHER I., “Dimensionnement des assemblages soudés en mécanosoudage, Calcul à la fatigue”, Soudage et Techniques convexes, p. 3-8, May-June 2000.
238
Metallurgy and Mechanics of Welding
[MAD 80] MADDOX S.J., Effect of misalignment on fatigue strength of transverse butt welded joints, IIS – Document XIII – 972-80, 1980. [MAD 98] MADDOX A., Private comm., 1998. [RAB 79] RABBE P., BLONDEAU R., CADIOU L., “Emploi des tôles à haute limite d’élasticité dans les constructions soudées sollicitées en fatigue”, Actes du Congrès sur les aciers à haute limite d’élasticité, Versailles, January 1979.
Chapter 7
Fracture Toughness of Welded Joints
7.1. Ductile fracture and brittle fracture In general, manufacturers dimension structures to avoid the risks of failure in service, by avoiding in particular any going beyond, even local, of the yield strength of the material. In spite of that, failures do occur, for various reasons: – exceptional load conditions; – progressive cracking related to fatigue, stress corrosion, hydrogen embrittlement; – behavioral change related to a transition of the ductile-brittle type, which originates in a temperature fall. Brittle fracture, due to the loss of plasticity, was first studied as early as the second half of the 19th century. With the development of welding and its application to the construction of largescale structures, a certain number of spectacular, often catastrophic, failures have occurred. Among the most famous examples we might recall bridge failures (at Berlin Zoo in 1936, in Rudesdorf and Hasselt in 1938) and storage tank failures. Of nearly 5,000 ships built by mechanized welding during World War II, a quarter of them presented important failures and more than 200 suffered catastrophic failure. The Schenectady oil tanker at anchor, without any particular excess loading, one night in winter 1942 is the classic example (see Figure 7.1). Chapter written by Marc BOUSSEAU.
240
Metallurgy and Mechanics of Welding
From immediately after the War, considerable work was undertaken in order to understand the phenomenon and to reduce the risks. The teams of the Naval Research Laboratory in Washington have been at the center of a great deal of work, particularly with W.S. Pellini and G.R. Irwin, which are still valid points of reference today. They concentrated on the study of the ductile-brittle transition temperature and the development of fracture mechanics concepts, taking into account weld defects. In parallel with the studies of mechanical engineers, metallurgists have devoted much energy to: – the development of steel types that are easier to weld (by lowering the carbon equivalent), offering higher levels of yield strength while having an increasingly lower ductile-brittle transition temperature; – the development of welding processes to reduce brittleness and the presence of defects.
Figure 7.1. Failure at anchor of the Schenectady tanker
Despite all these efforts, other failures continued to occur (bridges, pipelines, pressure vessels, ships, etc.). As Toyoda has demonstrated [TOY 00], a considerable amount of the damage noted at the time of the Kobe and Northbridge earthquakes was attributed to concomitant circumstances:
Fracture Toughness of Welded Joints
241
– raised stress load levels, to which residual stresses can be added; – presence of stress concentrations due to the geometry of the assemblies, possibly with the presence of defects in the form of cracks; – materials with a low resistance to in-service temperature. Within the International Institute of Welding (IIW), which meets annually, there is commission X whose work is devoted to the study of the failure of welded structures. The main themes tackled relate to operational suitability, taking account of heterogenities between the base metal and molten metal (characterized by mismatching) and the role of residual stresses. A working group was created with the aim, amongst other things, of analyzing the causes of failure in mechanized welded structures. The work of the IIW is relayed to France within the framework of the advisory committee of research into welding rupture, a mirror image of commission X. This advisory body (CCRS) receives the support of l’Institut de Soudure (French Institute of Welding) and la Société des Ingénieurs Soudeurs (SIS). 7.2. Evaluation of fracture risks in metallic materials The evaluation of the fracture risks of structural steels was initially tackled by means of the ductile-brittle transition temperature. Later, the introduction of the concept of toughness made it possible to judge the influence of a plane defect according to the load conditions. In all cases, tests have been developed in order to characterize the base materials. 7.2.1. Determination of the ductile-brittle transition temperature Initially, research was concerned with understanding the ductile-brittle transition of base materials, using the Charpy test with toughness test specimens and the Pellini, Batelle, Schnadt tests [SAN 74]. The impact bending test, which replaced the impact test or Charpy test, continues to be widely used to evaluate the ductile-brittle transition temperature. In general, the test-specimens are parallelepipedic bars (55x10x10 mm3) with a 45° V-shaped notch 2 mm deep. The fracture is obtained using a Charpy pendulum (see Figure 7.2). Some specimens are tested at various temperatures in order to plot the curves:
242
Metallurgy and Mechanics of Welding
– impact bending energy (expressed in J) according to the temperature (see Figure 7.3), – level of crystallinity according to the temperature, – lateral expansion (related to plastification) according to the temperature. From these curves, we can in particular determine the bending energy corresponding to the ductile stage as well as the temperatures corresponding to: – the ductile-brittle transition (Tt), – 50% of crystallinity, – the fracture energy at 28 J. In fact the transition temperature is not an intrinsic property of the material. It is established that this increases with: – increase in part thickness, – increase in the loading speed, – the increase in sharpness/angle at the notch bottom. K. Kalna [KAL 00] gives a formula making it possible to evaluate the influence of the transition temperature TTh for a structural element of thickness h: TT h
§ h· T 50 % 30 ln¨© 10 ¸¹
where T50% corresponds to the transition temperature for an impact bend test specimen 10 mm in thickness. Between the deformation speed H and the transition temperature there exists an expression of the type:
H
§ · ¨ Q ¸ A exp¨ A ¸ ¨ RT ¸ ¹ ©
where A is a constant, QA is the activation energy of the phenomenon, R is the constant of perfect gases and T is the absolute transition temperature.
Fracture Toughness of Welded Joints
243
Figure 7.2. Impact bend test specimen; from [NF 90]
Figure 7.3. Ductile-brittle transition curve; from [BAL 97]
Moderate in cost, the Charpy test continues to be widely used and is still, after 100 years in existence, the object of many studies – as the congress organized in 2001 on this topic testifies. At the beginning of the 1970s, work relating to the apparatus for impact bending testing was undertaken in order to highlight the various phases of fracture propagation by analysis of force-time graphs [SAN 69]. Since 1995, the working group “Instrumented Charpy” of the SF2M have led a study intended to numerically
244
Metallurgy and Mechanics of Welding
simulate the impact test by a finite element calculation in the brittle field. From these results, by using the local approach of the mechanic fracture, it is possible to evaluate the material’s toughness. The work of Rossol on pressure vessel steel 16MnNiMo5 constitutes an interesting contribution in this field [ROS 98]. Among the various fracture tests developed by Pellini [PEL 71], we will consider the drop weight test, which consists of dropping a mass from a given height on a specimen comprising a notched brittle weld deposit (see Figure 7.4). The specimen is subjected to bending and its deformation is limited. Under the effect of the shock the bead breaks, which creates a fine crack crossing the heat affected zone (HAZ). Depending on the temperature at which the test is carried out, the crack spreads to a greater or lesser extent in the base metal. We can, by a framework, determine the highest temperature leading to the fracture of the test specimen (see Figure 7.5). This temperature is called the NDT (nil ductility transition). With the original aim of forming steel for ship hulls and submarines, it was then applied to steels for vessels in nuclear installations. The standard defining the Pellini test underwent modifications with regard to the method of bead deposit [AST 95].
Figure 7.4. Dimensions of the Pellini test-piece; from [LEI 71]
Figure 7.5. The NDT lies between -20 and -30°C; from [LEI 71]
Fracture Toughness of Welded Joints
245
As for the Charpy test, studies have been carried out in order to record the load evolution during the impact [SAN 69], thereby to allow a finer analysis of the different fracture phases [FRO 82, WIE 99]. By the early 1970s IRSID had undertaken a systematic comparison between the results obtained from the various tests, considering a wide range of steel types. Correlations were established, showing that the classification of steels is modified little by the choice of tests [SAN 70, SAN 74]. Thus, between temperature NDT obtained by the Pellini test and the temperature giving an energy of 35 J/cm2 (TK 35), starting from 67 data, the following expression: (NDT) = -16 + 0.5l(TK35) is proposed, albeit with a rather low correlation coefficient (0.80). 7.2.2. Determination of a fracture criterion in the elastic linear field The development of the concepts of fracture mechanics at the beginning of the 1960s in the USA made it possible to take defect dimensions into account in the evaluation of the fracture risks. This was achieved by introducing the concept of stress intensity factor KI through the formula:
K I DV Sa where Dis the coefficient dependant on the geometry of the part and the crack, Vthenominal stress and a the dimension of the crack. The break occurs when KI reaches the critical value KIC. The La-Colle-sur-Loup Summer School of September 1970, which was devoted to the fracture process, marked the nascent interest of various sectors of French industry in this new branch of mechanics. The texts of the conferences gathered by D. François [FRA 72] are still used today as a reference in this field. The determination of the critical stress intensity factor KIC [AST 97] has been applied in various industrial sectors using high elastic limit steels. In France standard NFA 03-180 [NF 81], intended for iron and steel products, defines the testspecimens, the conditions under which they are taken, the conduct of tests and the analysis of results. To obtain a valid value KIC, various conditions must be fulfilled. In particular, when we are concerned with the extent of the plastic zone, this must be small compared to the dimensions of the test-specimen. As a result, in the case of
246
Metallurgy and Mechanics of Welding
ductile materials, it necessitates the use of large-sized specimens. Indeed, it is necessary that the thickness B is such that:
R p0.2 being the yield strength of the material. Strictly speaking, this standard applies only to homogenous steels. However, in the absence of specific documents, it has also been applied to other materials as well as to welded joints. Among the standardized test-pieces most commonly used, the bend test specimen and the compact tensile (CT) specimen should be mentioned and are illustrated in Figure 7.6. The mechanical notch is prolonged by a fatigue crack in order to obtain as low a radius as possible at the extremity. It is important that the crack has the same length on the two faces of the specimen and is of similar internal configuration.
Figure 7.6. Three point bend test and CT specimens; from [SAN 78]
Fracture Toughness of Welded Joints
247
The critical stress intensity factor KIC applies in the case where the plastic zone at the crack’s extremity is small compared to the structural dimensions and thus applies mainly in the case of materials with low ductility or ductile materials of significant thickness. Like the impact bending energy, the toughness of materials with a centered cubic structure varies according to temperature. It decreases with a fall in temperature; consequently, for a given defect failure can occur at a lower level of loading. Much work demonstrates that the load speed of application influences toughness. The curve KIC = f (temperature) is shifted towards the right when the load speed increases, as illustrated in Figure 7.7 (taken from a study of Sanz and Marandet) relating to pressure vessel steel 16 MnNiMo5 [SAN 78].
Figure 7.7. Influence of load speed and temperature on toughness; from [SAN 78]
Finding equivalence between the toughness and impact strength tests Right from the first tests to determine toughness using the concept of fracture mechanics, correlations have been sought, in particular between the values of KIC and those obtained by means of much less costly impact tests. Many expressions are presented and analyzed in [COL 97, MEE 88, SAN 78].
248
Metallurgy and Mechanics of Welding
As example, in the ductile field we can quote the expression of Rolfe and Novak, verified by IRSID on a wide range of steels, up to a yield strength of 1,720 MPa. It takes the form:
§ K Ic · ¸ with ¨ © Re ¹
2
in mm, KV in J and Re in N/mm2.
Correlations also exist between KIC and impact strength at the lower shelf of the transition zone. IRSID established two additional types of correlation: – between the transition temperature defined by the tests of KIC and impact strength, – between the values of KIC and KV. By regarding the following temperatures as transition temperatures: – TKIC = temperature for which KIC = 100 MPa.m1/2, – TK28 = temperature for which KV = 28 J (KCV = 35 J/cm2), the following correlation can be established, for steels whose crystallinity at temperature TK28 is always higher than 80-85%: TKIC = 1.40TK28 in °C The relation between KIC and KV obtained for values of KV lower than 80 J is expressed for steel as follows: 1
K IC
19 ( KV ) 2
with KIC in MPa.m1/2 and KV in J. From the impact strength curve according to temperature, it is possible to plot curve KIC according to the temperature.
Fracture Toughness of Welded Joints
249
7.2.3. Fracture criteria in the elasto-plastic field In order to evaluate the fracture risks related to the presence of defects in ductile materials, other criteria have been introduced. Among the most used we can quote: JIC, COD, CTOD, whose definitions are recalled in [FRA 96]. For metallic materials, standards have been established by ASTM and employed by AFNOR in order to define the conditions of taking and dimensioning specimens, the conditions of fatigue pre-cracking, the conduct of tests and the analysis of results. The specimens used are more or less comparable with those used for the determination of the critical stress intensity factor KIC. Rice’s J-integral The J-integral, still called Rice’s integral, is a contour integral which makes it possible to extend the concepts of elastic linear fracture mechanics to materials presenting a significant plastic deformation at the crack point. This fracture criterion is widely used in the nuclear field to evaluate the risks of ductile tearing. The test conditions are described in [AST 96, NF 87]. The specimens comprise lateral notches facilitating pre-cracking and possibly a chevron notch to facilitate crack initiation. In the case of CT specimens, the notch opening is measured straight along the loading line. During loading, carried out at constant opening speed, the force corresponding to the opening is recorded. The area under the F-d curve, up to the displacement corresponding to the interruption of the test, corresponds to an energy (see Figure 7.8) and is used to calculate J. At the end of the test, the test-piece is turned blue, by hot oxidation, before being broken. Examining the fracture topography makes it possible to evaluate the stable propagation amplitude 'Į. The points J-ǻa are transferred to a reference frame (see Figure 7.9). After checking the validity conditions, the line dJ/da is determined by linear regression and the values of J0 and J02 corresponding to the start of ductile fracture. The method of partial unloadings makes it possible to determine, in theory with only one specimen, the critical displacement JIC which corresponds to the beginning of stable cracking. Between JIC and KIC a relation exists in the form:
where Q is the Poisson coefficient and E the material’s elasticity modulus. JIC is expressed in J/m ² when KIC is expressed in MPa.m1/2.
250
Metallurgy and Mechanics of Welding
Figure 7.8. Loading curve and determination of energy U; from [NF 87]
COD The concept of COD (crack opening displacement) was developed in Great Britain to answer the in-service security issues of the offshore oil rigs built in the North Sea. The specimens used are comparable with those used in elastic linear fracture mechanics and a fatigue crack is developed.
Figure 7.9. Determination of the conventional values J0,2 and dJ/da; from [NF 87]
In the beginning, the test consisted of measuring the opening at the notch bottom,
G, according to the load applied. Bearing in mind the difficulty of taking this measurement, a method consisting of calculating G, beginning by measuring the
Fracture Toughness of Welded Joints
251
crack mouth opening by means of a knife edge extensometer, was proposed. This method is based on the assumption that a rotation center exists and will be difficult to determine. It results in uncertainty as to the value of G [SAN 78]. Assuming we have the COD, the dimension of the critical defect in a structure can be calculated starting from the expression suggested by F.M. Burdekin: a
where C
§G · C ¨¨ ¸¸ © eY ¹
1
§ e · 2S ¨ ¨ e ¸¸ © Y¹
2
if
e is the real deformation undergone by the structure in the vicinity of the defect and eȖ the deformation at the yield strength. IRSID has shown that this method resulted in adopting excessive safety margins. CTOD Further development has continued, particularly in Anglo-Saxon countries and Japan, leading to CTOD (crack tip opening displacement) testing. The experimental conditions are defined in [AST 93, JWE 97, NF 87]. The force-opening curve is plotted until the test-specimen fractures or, failing this, it is stopped when beyond the load curve maximum. The curve is exploited in accordance with standard BS 7448 Part 1 [AST 93, NF 87]. According to the nature of the material, various types of curves can be obtained (see Figure 7.10). The plastic component Vp of the total opening V is obtained by tracing a straight line parallel with the linear part of the load curve. This component Vp is signified by VC, VI, VU or Vm according to the characteristic point considered.
252
Metallurgy and Mechanics of Welding
Figure 7.10. Various types of recordings variations in force applied according to the notch opening; from [NF 87]
For curves a and b, the force applied increases in a steady way with the opening of the notch mouth, until initiating an abrupt unstable crack propagation, which is not preceded by a stable propagation. The value of GC is given starting from the point of coordinates (FC, VC). In the three other cases, where the unstable propagation or the maximum force of plastic instability, is preceded by a certain stable propagation, the critical values GU or Gm of the CTOD are obtained, respectively starting from the points (FU, VU) or (Vm, Fm). The existence of a stable crack propagation preceding a possible brutal rupture can be highlighted a posteriori by examining the fracture topography. In all cases the critical values are calculated by means of the formula:
with:
K
F
1
BW 2
Y
Fracture Toughness of Welded Joints
253
Y being a function of a W , a0 the useful overall length of the initial defect, and z the distance between the knife blades and the loading axis in the case of a CT specimen. E, R p0.2 and Q are respectively the elasticity modulus, yield strength and the Poisson coefficient of the material. 7.3. Evaluation of fracture risks in welded joints The evaluation methods used to characterize welded joints are comparable with those implemented to characterize basic materials, except for the added difficulty taking a sample involved with heterogenities of the weld bead. 7.3.1. Heterogenities of the weld bead To assemble one or two materials by welding with or without filler (electron beam or laser beam welding for example) is a complex metallurgical operation which engenders many heterogenities: – chemical, the filler product is often different in composition from that of the materials to be assembled. The dilution effects in the bond zones are an additional factor;
Figure 7.11. Taking of test-specimens in a welded joint; from [ANS 92]
254
Metallurgy and Mechanics of Welding
Figure 7.12. Various possible notch orientations with regard to the weld bead; from [ANS 92]
Figure 7.13. X-shaped bead
– metallurgical, related to the number of heating and cooling phases depending on the number of passes; – mechanical, the behavior of the bead being different from that of the base materials. This type of heterogenity is referred to by Anglo-Saxons as mismatching. It is characterized by the relationship M between the yield strength of the fusion zone and the yield strength of the base material:
where
M
V YZ V YB
V YZ
is the yield strength of the HAZ and
V YB
that of the base metal.
Fracture Toughness of Welded Joints
255
If M >1 the term used is overmatching and, in the contrary case, undermatching: – geometric; taking into account the joint preparations and the shape of the beads (stress concentrations); – possible defects; planar or volumetric, internal or emerging surfaces which reduce the effective cross section. To these heterogenities we can add residual stresses, which are a consequence of the juxtaposition of zones brought up to very different temperatures, metallurgical transformations and restrictions of various significance due to clamping. 7.3.2. Conditions of specimen taking The transposition of the preceding tests to the welded joints must take account of the zones to characterize: fusion zone or HAZ. Figure 7.11 illustrates the most commonly used conditions of specimen removal to evaluate the fracture sensitivity of the fusion zone. In general, the notch is positioned in the middle of the cord with various possible orientations (see Figure 7.12). The determination of HAZ toughness is much more problematic, taking into account the geometry of the weld bead. A crack machined parallel to the bead axis encompasses more or less significant proportions of the HAZ, the remainder being made up of the base metal (see Figure 7.13). To mitigate this disadvantage, at least for the laboratories, K or half K-shaped specimens can be taken (see Figure 7.14), which makes it possible to have a crack located entirely in the HAZ.
Figure 7.14. Half K-shaped bead
256
Metallurgy and Mechanics of Welding
However, in spite of this method, the HAZ is far from being homogenous, as can be seen for example in the work of Toyoda [TOY 91]. It is made up of more or less brittle microstructures which are formed at the time of the various thermal cycles (see Figure 7.15) as will be observed later on (see section 7.4.4).
Figure 7.15. Various types of microstructures found in the HAZ according to the thermal cycles; from [TOY 89]
In certain cases, the test is carried out on a welded sheet 200 mm wide or more, a fatigue crack being developed either in the bead or in the HAZ [KOC 00]. Such testspecimens are in particular used within the framework of the Brite-Euram project ASsessment of quality off POwer beam Welded joints (ASPOW). This project aims at establishing recommendations for the characterization of the joints welded by the processes with high density of energy (electron beam and laser beam) which present a narrow bead with significant property gradients: overmatching for structural steels and undermatching for aluminum alloys. 7.3.3. Determination of the ductile-brittle transition temperature Concerning the determination of the energy in impact bend tests, standard NF IN 10045-1 [NF 90] defines dimensions and the conditions of sample taking (notch position compared to the FZ or the HAZ). In general, as for the characterization of
Fracture Toughness of Welded Joints
257
basic material, the impact bend-test specimen is a parallelepipedic bar (55 u 10 u 10 mm3) with a 45° V-shaped notch 2 mm in depth. The standard envisages the possibility of using test specimens of reduced thickness (7.5 mm or 5 mm). Following the failures which have occurred during the Kobe and Northbridge earthquakes, impact bend test results showed fracture energies of approximately 10 J at room temperature, for the base metal and the fusion zone, which is very low [TOY 00]. Of the rare plates from Liberty ships which have been examined, energies from 8 to 9 J for the temperature at the time of the accident have been found, whereas energy reached 21 J in the remoter zones [SAN 74]. In general, it is necessary that the ductile-brittle transition temperature is lower than the minimum service temperature. Following the work of a group of experts, made up from members of Commission X of the IIW, chaired by H.H. Campbell, recommendations were made for the mechanized welded constructions erected in zones where seismic risks exist [CAM 00]. The simplest procedure gives, for various risk levels, the impact bend energy values to be reached at a temperature corresponding to the minimum temperature of use (see Table 7.1). According to the specimen taking conditions and the position of the notch bottom in relation to the FZ or the HAZ, the results can vary significantly, as some of the impact bend test results obtained at various temperatures by N. Gubeljak [GUB 99] show. KV (J) Test temperature = Min. service temperature KV>100
Risk of brittle fracture Breakage improbable
47